Beam Diameter Dependence of Performance in Thick-Layer and High-Power Selective Laser Melting of Ti-6Al-4V
A 400 W high-power laser was used to fabricate 200-µm-thick Ti-6Al-4V samples to evaluate the effects of small (50 μm) and large (200 μm) beam diameter on density, microstructure and mechanical properties. A series of single-track experiments demonstrated that it was challenging for the small-beam l...
Autores principales: | Shi, Wentian, Liu, Yude, Shi, Xuezhi, Hou, Yanjun, Wang, Peng, Song, Guohua |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2018
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6073386/ https://www.ncbi.nlm.nih.gov/pubmed/30022002 http://dx.doi.org/10.3390/ma11071237 |
Ejemplares similares
-
Performance of High Layer Thickness in Selective Laser Melting of Ti6Al4V
por: Shi, Xuezhi, et al.
Publicado: (2016) -
Research on High Layer Thickness Fabricated of 316L by Selective Laser Melting
por: Wang, Shuo, et al.
Publicado: (2017) -
Experimental Research on Variable Parameter Forming Process for Forming Specimen of TC4 Titanium Alloy by Selective Laser Melting
por: Liu, Yude, et al.
Publicado: (2022) -
Single tracks data obtained by selective laser melting of Ti6Al4V with a small laser spot diameter
por: Vaglio, Emanuele, et al.
Publicado: (2020) -
Directionally-Dependent Mechanical Properties of Ti6Al4V Manufactured by Electron Beam Melting (EBM) and Selective Laser Melting (SLM)
por: Pasang, Tim, et al.
Publicado: (2021)