Optimized Procedure for Determining the Adsorption of Phosphonates onto Granular Ferric Hydroxide using a Miniaturized Phosphorus Determination Method

This paper introduces a procedure to investigate the adsorption of phosphonates onto iron-containing filter materials, particularly granular ferric hydroxide (GFH), with little effort and high reliability. The phosphonate, e.g., nitrilotrimethylphosphonic acid (NTMP), is brought into contact with the GFH in a rotator in a solution buffered by an organic acid (e.g., acetic acid) or Good buffer (e.g., 2-(N-morpholino)ethanesulfonic acid) [MES] and N-cyclohexyl-2-hydroxyl-3-aminopropanesulfonic acid [CAPSO]) in a concentration of 10 mM for a specific time in 50 mL centrifuge tubes. Subsequently, after membrane filtration (0.45 µm pore size), the total phosphorus (total P) concentration is measured using a specifically developed determination method (ISO(mini)). This method is a modification and simplification of the ISO 6878 method: a 4 mL sample is mixed with H(2)SO(4) and K(2)S(2)O(8) in a screw cap vial, heated to 148-150 °C for 1 h and then mixed with NaOH, ascorbic acid and acidified molybdate with antimony(III) (final volume of 10 mL) to produce a blue complex. The color intensity, which is linearly proportional to the phosphorus concentration, is measured spectrophotometrically (880 nm). It is demonstrated that the buffer concentration used has no significant effect on the adsorption of phosphonate between pH 4 and 12. The buffers, therefore, do not compete with the phosphonate for adsorption sites. Furthermore, the relatively high concentration of the buffer requires a higher dosage concentration of oxidizing agent (K(2)S(2)O(8)) for digestion than that specified in ISO 6878, which, together with the NaOH dosage, is matched to each buffer. Despite the simplification, the ISO(mini) method does not lose any of its accuracy compared to the standardized method.