Fabrication of Hierarchical ZnO@NiO Core–Shell Heterostructures for Improved Photocatalytic Performance

ZnO@NiO core–shell heterostructures with high photocatalytic efficiency and reusability were prepared via electrochemical deposition on carbon fiber cloth substrates. Their photocatalytic properties were investigated by measuring the degradation of rhodamine B and methyl orange (MO) under ultraviolet light irradiation. The photodegradation efficiency of the ZnO@NiO heterostructures toward both dyes was better than those of the pure ZnO nanorods and NiO nanosheets. The higher performance could be attributed to the formation of p–n heterojunction between ZnO and NiO. Especially, the ZnO@NiO heterostructure formed upon deposition of NiO for 10 min degraded 95% of MO under ultraviolet light irradiation for 180 min. The high photodegradation efficiency of the ZnO@NiO heterostructures was also attributed to the high separation efficiency of photogenerated carriers, as confirmed by the higher photocurrent of the ZnO@NiO heterostructures (eightfold) when compared with that of the pure ZnO nanorods. Moreover, the high photodegradation efficiency of the ZnO@NiO heterostructures was maintained over three successive degradation experiments and decreased to 90% after the third cycle. ELECTRONIC SUPPLEMENTARY MATERIAL: The online version of this article (10.1186/s11671-018-2676-1) contains supplementary material, which is available to authorized users.