Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys

Aluminum alloys are widely used as first-choice materials for lightweight automotive applications. It is important that an alloy have a balance between strength and formability. In this study, the alloys were melted, cast, hot rolled, and cold rolled into 1 mm-thick sheets. The microstructure, mecha...

Descripción completa

Detalles Bibliográficos
Autores principales: Li, Yong, Gao, Guanjun, Wang, Zhaodong, Di, Hongshuang, Li, Jiadong, Xu, Guangming
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2018
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6316410/
https://www.ncbi.nlm.nih.gov/pubmed/30572642
http://dx.doi.org/10.3390/ma11122591
_version_ 1783384523331862528
author Li, Yong
Gao, Guanjun
Wang, Zhaodong
Di, Hongshuang
Li, Jiadong
Xu, Guangming
author_facet Li, Yong
Gao, Guanjun
Wang, Zhaodong
Di, Hongshuang
Li, Jiadong
Xu, Guangming
author_sort Li, Yong
collection PubMed
description Aluminum alloys are widely used as first-choice materials for lightweight automotive applications. It is important that an alloy have a balance between strength and formability. In this study, the alloys were melted, cast, hot rolled, and cold rolled into 1 mm-thick sheets. The microstructure, mechanical properties, and precipitation behavior of Al–Mg–Si–1.0 wt %-Zn alloys with Mg/Si ratios of 0.5, 1, and 2 after solution treatment were studied using optical and electron microscopy, a tensile test, the Vickers hardness test, and differential scanning calorimetry. The results showed that a high density and number of Al–Fe–Si particles were observed in the matrix, thus causing the formation of more homogeneous and smaller recrystallized grains after treatment with the solution. In addition, a higher volume fraction of cube(ND) and P-types texture components formed during solution treatment. Also, a high r value and excellent deep drawability were achieved in the medium-Mg/Si-ratio alloy. The formation of denser strengthening precipitates led to a better paint-bake hardening effect in comparison with the other two alloys. Furthermore, the precipitation kinetics were enhanced by the addition of Si, and the addition of Zn did not alter the precipitation sequence of the Al–Mg–Si alloy. The dual-phase strengthening effect was not achieved in the studied alloys during paint-bake treatment at 175 °C.
format Online
Article
Text
id pubmed-6316410
institution National Center for Biotechnology Information
language English
publishDate 2018
publisher MDPI
record_format MEDLINE/PubMed
spelling pubmed-63164102019-01-08 Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys Li, Yong Gao, Guanjun Wang, Zhaodong Di, Hongshuang Li, Jiadong Xu, Guangming Materials (Basel) Article Aluminum alloys are widely used as first-choice materials for lightweight automotive applications. It is important that an alloy have a balance between strength and formability. In this study, the alloys were melted, cast, hot rolled, and cold rolled into 1 mm-thick sheets. The microstructure, mechanical properties, and precipitation behavior of Al–Mg–Si–1.0 wt %-Zn alloys with Mg/Si ratios of 0.5, 1, and 2 after solution treatment were studied using optical and electron microscopy, a tensile test, the Vickers hardness test, and differential scanning calorimetry. The results showed that a high density and number of Al–Fe–Si particles were observed in the matrix, thus causing the formation of more homogeneous and smaller recrystallized grains after treatment with the solution. In addition, a higher volume fraction of cube(ND) and P-types texture components formed during solution treatment. Also, a high r value and excellent deep drawability were achieved in the medium-Mg/Si-ratio alloy. The formation of denser strengthening precipitates led to a better paint-bake hardening effect in comparison with the other two alloys. Furthermore, the precipitation kinetics were enhanced by the addition of Si, and the addition of Zn did not alter the precipitation sequence of the Al–Mg–Si alloy. The dual-phase strengthening effect was not achieved in the studied alloys during paint-bake treatment at 175 °C. MDPI 2018-12-19 /pmc/articles/PMC6316410/ /pubmed/30572642 http://dx.doi.org/10.3390/ma11122591 Text en © 2018 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).
spellingShingle Article
Li, Yong
Gao, Guanjun
Wang, Zhaodong
Di, Hongshuang
Li, Jiadong
Xu, Guangming
Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title_full Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title_fullStr Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title_full_unstemmed Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title_short Effects of the Mg/Si Ratio on Microstructure, Mechanical Properties, and Precipitation Behavior of Al–Mg–Si–1.0 wt %-Zn Alloys
title_sort effects of the mg/si ratio on microstructure, mechanical properties, and precipitation behavior of al–mg–si–1.0 wt %-zn alloys
topic Article
url https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6316410/
https://www.ncbi.nlm.nih.gov/pubmed/30572642
http://dx.doi.org/10.3390/ma11122591
work_keys_str_mv AT liyong effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys
AT gaoguanjun effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys
AT wangzhaodong effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys
AT dihongshuang effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys
AT lijiadong effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys
AT xuguangming effectsofthemgsiratioonmicrostructuremechanicalpropertiesandprecipitationbehaviorofalmgsi10wtznalloys