Preparation and Properties of Acetoacetic Ester-Terminated Polyether Pre-Synthesis Modified Phenolic Foam

In the present study, acetoacetic ester-terminated polyether was selected as a modifier to prepare a new type of polyether phenolic resin, which was successfully prepared by pre-synthesis modification. It is used to prepare interpenetrating cross-linked network structure modified phenolic foam with...

Descripción completa

Detalles Bibliográficos
Autores principales: Ge, Tiejun, Tang, Kaihong, Tang, Xiaojun
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2019
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6384588/
https://www.ncbi.nlm.nih.gov/pubmed/30678150
http://dx.doi.org/10.3390/ma12030334
Descripción
Sumario:In the present study, acetoacetic ester-terminated polyether was selected as a modifier to prepare a new type of polyether phenolic resin, which was successfully prepared by pre-synthesis modification. It is used to prepare interpenetrating cross-linked network structure modified phenolic foam with excellent mechanical properties. Fourier transform infrared spectroscopy (FT-IR) and nuclear magnetic resonance ((1)H NMR, (13)C NMR) were used to characterize the molecular structure of the polyether phenolic resin. The results showed that the acetoacetic ester-terminated polyether successfully modified the phenolic resin and introduced a polyether skeleton into the resin structure. The effect of changing the added amount of acetoacetic ester-terminated polyether from 10% to 20% of the phenol content on the mechanical properties and microstructure of the modified phenolic foam was investigated. The results showed that when the amount of acetoacetic ester-terminated polyether was 16% the amount of phenol, this resulted in the best toughness of the modified foam, which had a bending deflection that could be increased to more than three times that of the base phenolic foam. The modified phenolic foam cell diameter was reduced by 36.3%, and the distribution was more uniform, which formed a denser network structure than that of the base phenolic foam. The bending strength was increased by 0.85 MPa, and the pulverization rate was as low as 1.3%.