Crack Healing and Mechanical Properties Recovery in SA 508–3 Steel

Internal cracks could be healed under the process of hot plastic deformation. In this study, mechanical properties recovery after crack healing in SA 508–3 steel were investigated. Microstructures of the crack healing zones were observed using an optical microscope (OM) and electron back scattered d...

Descripción completa

Detalles Bibliográficos
Autores principales:	Qiu, Yao, Xin, Ruishan, Luo, Jianbin, Ma, Qingxian
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2019
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6471081/ https://www.ncbi.nlm.nih.gov/pubmed/30884904 http://dx.doi.org/10.3390/ma12060890

Ejemplares similares

The Effect of the Microstructure Formed in the Forging–Healing Process on the Mechanical Properties of Heavy Forgings
por: Liu, Qianjun, et al.
Publicado: (2023)

Effect of microstructure on the impact toughness and temper embrittlement of SA508Gr.4N steel for advanced pressure vessel materials
por: Yang, Zhiqiang, et al.
Publicado: (2018)

Healing of Fatigue Crack in 1045 Steel by Using Eddy Current Treatment
por: Yang, Chuan, et al.
Publicado: (2016)

Effect of thrombin peptide 508 (TP508) on bone healing during distraction osteogenesis in rabbit tibia
por: Amir, Lisa R., et al.
Publicado: (2007)

Recovery of ΔF508-CFTR Function by Citrate
por: Borkenhagen, Beatrice, et al.
Publicado: (2022)

Strategies Regarding High-Temperature Applications w.r.t Strength, Toughness, and Fatigue Life for SA508 Alloy
por: Abdullah, Muhammad Raies, et al.
Publicado: (2021)

Temperature Experiment and Parameter Optimization of Cemented Carbide Tool in Milling 508III Steel
por: Cheng, Yaonan, et al.
Publicado: (2023)

Effect of autogenous crack self-healing on mechanical strength recovery of cement mortar under various environmental exposure
por: Suleiman, A. R., et al.
Publicado: (2021)

Molar Ratio Effect of Sodium to Chloride Ions on the Electrochemical Corrosion of Alloy 600 and SA508 in HCl + NaOH Mixtures
por: Hur, Do Haeng, et al.
Publicado: (2020)

Recovery of Chloride Penetration Resistance of Cement-Based Composites Due to Self-Healing of Cracks
por: Yoo, Kyung Suk, et al.
Publicado: (2021)

Analysis of Internal Crack Healing Mechanism under Rolling Deformation
por: Gao, Haitao, et al.
Publicado: (2014)

Healing of Fatigue Crack by High-Density Electropulsing in Austenitic Stainless Steel Treated with the Surface-Activated Pre-Coating
por: Hosoi, Atsushi, et al.
Publicado: (2013)

Effect of Titanium and Boron Microalloying on Sulfide Stress Cracking in C110 Casing Steel
por: Luo, Ming, et al.
Publicado: (2020)

Effect of Bacillus subtilis on mechanical and self-healing properties in mortar with different crack widths and curing conditions
por: Yamasamit, Nattapong, et al.
Publicado: (2023)

Crack Detection of Threaded Steel Rods Based on Ultrasonic Guided Waves
por: Peng, Kunhong, et al.
Publicado: (2022)

Influence of the Thermal Cutting Process on Cracking of Pearlitic Steels
por: Tuz, Lechosław, et al.
Publicado: (2021)

Susceptibility of High-Manganese Steel to High-Temperature Cracking
por: Fojt-Dymara, Gabriela, et al.
Publicado: (2022)

Structural reorganization and crack-healing properties of hydrogels based on dynamic diselenide linkages
por: Xu, Hao, et al.
Publicado: (2020)

Comparison of Mechanical and Crack-Healing Properties of PE-PVA Hybrid Fiber-Reinforced SHCCs in Natural and Underwater Conditions
por: Park, Se-Eon, et al.
Publicado: (2022)

Quantitative Detection of Cracks in Steel Using Eddy Current Pulsed Thermography
por: Shi, Zhanqun, et al.
Publicado: (2018)

Influence of TiN Inclusions and Segregation Bands on the Mechanical Properties and Delayed Crack in Thick NM550 Wear-Resistant Steel
por: Sun, Haoran, et al.
Publicado: (2023)

Effect of Healing Agents on Crack Healing of Asphalt and Asphalt Mortar
por: Pan, Changluan, et al.
Publicado: (2018)

Comparison of the Mechanical Properties and Crack Expansion Mechanism of Different Content and Shapes of Brass-Coated Steel Fiber-Reinforced Ultra-High-Performance Concrete
por: Jiang, Yanli, et al.
Publicado: (2023)

Detection of Steel Fatigue Cracks with Strain Sensing Sheets Based on Large Area Electronics
por: Yao, Yao, et al.
Publicado: (2015)

Answer to the question page 508
Publicado: (2012)

Steel Corrosion Evaluation of Basalt Fiber RPC Affected by Crack and Steel-Concrete Interface Damage Using Electrochemical Methods
por: Liu, Hanbing, et al.
Publicado: (2020)

Full strength and toughness recovery after repeated cracking and healing in bone-like high temperature ceramics
por: Osada, Toshio, et al.
Publicado: (2020)

Microstructure and Properties of ER50-6 Steel Fabricated by Wire Arc Additive Manufacturing
por: Hu, Qingxian, et al.
Publicado: (2021)

Effect of Tempering Temperature on Microstructure and Sulfide Stress Cracking of 125 Ksi Grade Casing Steel
por: Luo, Ming, et al.
Publicado: (2022)

Initiation and growth kinetics of solidification cracking during welding of steel
por: Aucott, L., et al.
Publicado: (2017)

Analysis of Fatigue Crack Paths in Cold Drawn Pearlitic Steel
por: Toribio, Jesús, et al.
Publicado: (2015)

Post-Cracking Capacity of Glass Beams Reinforced with Steel Fibers
por: Corradi, Marco, et al.
Publicado: (2019)

Acoustic Emission Monitoring of Fatigue Crack Growth in Hadfield Steel
por: Shi, Shengrun, et al.
Publicado: (2023)

Solidification Crack Evolution in High-Strength Steel Welding Using the Extended Finite Element Method
por: Chen, Zhanglan, et al.
Publicado: (2020)

Influence of Steel Plates and Studs on Shrinkage Behavior and Cracking Potential of High-Performance Concrete
por: Huang, Lepeng, et al.
Publicado: (2019)

A Review on Cementitious Self-Healing and the Potential of Phase-Field Methods for Modeling Crack-Closing and Fracture Recovery
por: Yang, Sha, et al.
Publicado: (2020)

508 Retrospective Review of Early Pulmonary Mechanics After Inhalation Injury
por: Lam, Eric, et al.
Publicado: (2023)

Crack-free in situ heat-treated high-alloy tool steel processed via laser powder bed fusion: microstructure and mechanical properties
por: Bergmueller, Simon, et al.
Publicado: (2022)

Study on micro crack propagation mechanism of ferrite–pearlite gas transmission pipeline steel with lamellar structure
por: Xu, Taolong, et al.
Publicado: (2022)

Research on the Fatigue Crack Growth Behavior of a Zr/Ti/Steel Composite Plate with a Crack Normal to the Interface
por: Zhou, Binbin, et al.
Publicado: (2023)

Cannot write session to /tmp/vufind_sessions/sess_rdru445todj8sd1e1mmpef5bkb