Natural Advantages of Preparation of Composites from Minerals: Effect of Bauxite Addition on the Microstructures and Properties of Fe-Al(2)O(3) Based Composites

Fe-Al(2)O(3) composites were prepared by pressureless sintering, using Bayan Obo iron concentrate and bauxite as the main raw materials, activated carbon was added as the reducing agent. The effects of different bauxite additions on the phase composition, microstructures, mechanical properties, and the corrosion-resistance were investigated. The results show that the average grain size of alumina decreased as the bauxite content increased. In addition, bauxite contains TiO(2), CaO, and MgO, that can form a liquid phase at high temperature, causing the heat capacity of the micro-zone around the metal phase to be different, which leads to a change of undercooling and further affects the dislocation density of the metal phase. The plastic deformation ability of the metal phase can be improved with the low dislocation density. Fracture mechanism analysis indicated that the metal phase absorbed energy through plastic deformation. The optimum performance of the sample was as follows: the flexural strength was 310 MPa, the hardness 12.14 GPa, the alkali resistance 98.32%, and the acid resistance 95.44%.