Mechanical Characterization of Thermoplastic Aligner Materials: Recommendations for Test Parameter Standardization
BACKGROUND: Understanding of the different mechanical properties of thermoplastic materials is essential for a successful aligner treatment and further developments. However, data of previous material testing studies are scarcely comparable. Aim of the current study was to evaluate the different tes...
Autores principales: | , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Hindawi
2019
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6560334/ https://www.ncbi.nlm.nih.gov/pubmed/31275537 http://dx.doi.org/10.1155/2019/8074827 |
Sumario: | BACKGROUND: Understanding of the different mechanical properties of thermoplastic materials is essential for a successful aligner treatment and further developments. However, data of previous material testing studies are scarcely comparable. Aim of the current study was to evaluate the different test parameters to lay the foundations for guidelines for future, more standardized three-point-bending aligner material tests. MATERIALS AND METHODS: Several parameters concerning the specimen preparation and experimental three-point-bending setup were varied. The specimens were collected from polyethylene terephthalate glycol (PET-G) Duran® foils with different thicknesses. Both raw foils and foils thermoformed using different geometrical forms were investigated. The three-point-bending tests were performed using span lengths of 8 and 16 mm and variable deflection ranges between 0.1 and 0.2 mm. The influence of water storage on the bending forces was studied using unloaded and loaded specimens. Experimental results were validated using a beam cantilever mathematical model. RESULTS: Local macroscopic cracks after long-term loading could be avoided by keeping the deflections within a thickness-dependent individual range. The mathematical calculations confirmed that these individual deflection ranges lead to local stresses between 14 and 18 MPa. Constantly loaded specimens immersed for 24 hours in water showed a decrease of the bending force by 50%. This reduction was much smaller for the unloaded specimens (14%). CONCLUSION: During clinical aligner therapy, very small bending deflections are combined with small distances between the tooth surface regions supporting the aligner. In vitro aligner material testing by three-point bending should consider these geometrical aspects, while keeping the material stresses in a range between 14 and 18 MPa to avoid local microcracks. Considering these aspects, thickness-dependent deflections were established for three-point bending of the PET-G specimen for a span length of 8 mm. We recommend the application of these test parameters in future aligner material studies to achieve valid and comparable test results. |
---|