Ethylenediamine-Catalyzed Preparation of Nitrogen-Doped Hierarchically Porous Carbon Aerogel under Hypersaline Condition for High-Performance Supercapacitors and Organic Solvent Absorbents

The simple and cost-efficient preparation of high-performance nitrogen-doped carbon aerogel (N-CA) for supercapacitors and other applications is still a big challenge. In this work, we have presented a facile strategy to synthesize hierarchically porous N-CA, which is based on solvothermal polymerization of phenol and formaldehyde under hypersaline condition with ethylenediamine (EDA) functioning as both a catalyst and a nitrogen precursor. Benefited from the catalytic effect of EDA on the polymerization, the obtained N-CA has a predominant amount of micropores (micropore ratio: 52%) with large specific surface area (1201.1 m(2)·g(−1)). In addition, nitrogen doping brings N-CA enhanced wettability and reduced electrochemical impedance. Therefore, the N-CA electrode shows high specific capacitance (426 F·g(−1) at 1 A·g(−1) in 0.5 M H(2)SO(4)) and excellent cycling stability (104% capacitance retention after 10,000 cycles) in three-electrode systems. Besides, a high energy density of 32.42 Wh·kg(−1) at 800 W·kg(−1) can be achieved by symmetric supercapacitor based on the N-CA electrodes, showing its promising application for energy storage. Furthermore, N-CA also exhibits good capacity and long recyclability in the absorption of organic solvents.