The Influence of Welding Process Parameters on Pore Formation in Pulsed Laser-Welded Vacuum Plate Glazing

To explore the mechanism of the pore formation in the laser-welded vacuum plate glazing sealing layer, a vacuum plate glazing laser side sealing test was carried out. The influence of the pulse current, pulse duration time, pulse frequency and welding speed on the pores of the sealing layer was stud...

Descripción completa

Detalles Bibliográficos
Autores principales: Zhang, Shanwen, Li, Chong, Miao, Hong, He, Qiang
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2019
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6600737/
https://www.ncbi.nlm.nih.gov/pubmed/31159507
http://dx.doi.org/10.3390/ma12111790
Descripción
Sumario:To explore the mechanism of the pore formation in the laser-welded vacuum plate glazing sealing layer, a vacuum plate glazing laser side sealing test was carried out. The influence of the pulse current, pulse duration time, pulse frequency and welding speed on the pores of the sealing layer was studied by means of scanning electron microscopy (SEM) and metallographic microscopy, and the cause of the pores is analyzed. The results show that the porosity decreases with the increase of the pulse current. When the pulse current is 160 A, the pores are the fewest and smallest, and the porosity is only 0.1%. The porosity of the sealing layer decreases first and then increases with the increase of the pulse duration time. The porosity decreases first and then increases with the increase of the pulse frequency. When the pulse frequency is 18 Hz, the porosity is the least, at only 0.08%. The porosity of the sealing layer increases with the increase of the welding speed. When the welding speed is 80, 90, 100 and 110 mm/min, the porosity is 0.02, 0.08, 0.63 and 0.89%, respectively. These studies can provide a theoretical basis for laser sealing manufacturing of vacuum plate glazing.