A technological combination of lead-glaze and calcium-glaze recently found in China: Scientific comparative analysis of glazed ceramics from Shangyu, Zhejiang Province

To study the relationship between the glazed pottery from southern China and the lead-glazed pottery in northern China in the Han Dynasty (202BC-220AD), 34 samples unearthed from Shangyu(上虞), Zhejiang Province have been studied by LA-ICP-AES, SEM/EDS and XRD. The results showed that these samples included the typical lead-glazed pottery, the proto-porcelain and the glazed pottery using both lead and calcium as glaze fluxing agents. Previously, the lead-glazed pottery type was considered as the main northern products during the Han dynasty while the calcium-glazed pottery type or the proto-porcelain was the representative of the south of China. However, apart from the two typical types above, a new variety of glaze categorized as the calcium-lead glaze was discovered in the samples from Shangyu. This indicates that there were technology exchanges and amalgamation of lead-glaze and calcium-glaze between the south and the north during the Han Dynasty. As a result, a new type of glazed potteries with both features was created, which had a more beautiful appearance than the proto-porcelain but perhaps had some undesirable aspects. The manufacturing process of the new variety might also lay foundations for the invention of celadon.