On the Formation of AlNiCo Nano-Quasicrystalline Phase during Mechanical Alloying through Electroless Ni-P Plating of Starting Particles

A new strategy was applied to develop nano-quasicrystalline phase in well-known AlNiCo ternary system. This approach was based on electroless Ni-P plating of the starting powders and subsequent ball milling in a protective atmosphere without additional annealing or sintering processes. Microstructur...

Descripción completa

Detalles Bibliográficos
Autores principales: Hosseini, Seyedmehdi, Novák, Pavel
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2019
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6678659/
https://www.ncbi.nlm.nih.gov/pubmed/31323737
http://dx.doi.org/10.3390/ma12142294
Descripción
Sumario:A new strategy was applied to develop nano-quasicrystalline phase in well-known AlNiCo ternary system. This approach was based on electroless Ni-P plating of the starting powders and subsequent ball milling in a protective atmosphere without additional annealing or sintering processes. Microstructural evolution and phase transformation of both raw and coated particles were analyzed by scanning electron microscope (SEM) and X-ray diffraction (XRD), respectively. After 360 min of mechanical alloying, the peaks demonstrating the formation of nano-quasicrystalline phase appeared in XRD pattern of the coated powders, while those in mechanically alloyed raw powders remained mostly unchanged. The formation of nano-quasicrystalline phase in the vicinity of the primary elements was also confirmed by the corresponding selected area diffraction patterns, and images generated by transmission electron microscope (TEM).