Effects of Transverse Crack on Chloride Ions Diffusion and Steel Bars Corrosion Behavior in Concrete under Electric Acceleration

Cracks greatly impact the durability of concrete structures due to their influence on the migration of chloride ions and the corrosion process of steel bars. This study investigates the effects of transverse cracks on chloride diffusion and the corrosion behavior of two types of steel bars (low carb...

Descripción completa

Detalles Bibliográficos
Autores principales:	Du, Fengyin, Jin, Zuquan, Xiong, Chuansheng, Yu, Yong, Fan, Junfeng
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2019
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6696064/ https://www.ncbi.nlm.nih.gov/pubmed/31387218 http://dx.doi.org/10.3390/ma12152481

Ejemplares similares

Monitoring Corrosion of Steel Bars in Reinforced Concrete Structures
por: Verma, Sanjeev Kumar, et al.
Publicado: (2014)

Macrocell Corrosion of Steel in Concrete under Carbonation, Internal Chloride Admixing and Accelerated Chloride Penetration Conditions
por: Jiang, Zhilu, et al.
Publicado: (2021)

Modelling of Corrosion-Induced Concrete Cover Cracking Due to Chloride Attacking
por: Lun, Pei-Yuan, et al.
Publicado: (2021)

Fractal Characterization of Non-Uniform Corrosion of Steel Bars in Concrete Beams after Accelerated depassivation and Seven-Year Natural Corrosion
por: Jiang, Haoyu, et al.
Publicado: (2019)

Self-immunity microcapsules for corrosion protection of steel bar in reinforced concrete
por: Wang, Yanshuai, et al.
Publicado: (2015)

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
por: Singh Raman, R. K., et al.
Publicado: (2014)

Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments
por: Yeh, Chun-Ping, et al.
Publicado: (2020)

Properties of Concretes Incorporating Recycling Waste and Corrosion Susceptibility of Reinforcing Steel Bars
por: Blikharskyy, Zinoviy, et al.
Publicado: (2021)

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution
por: Jiang, Jin-yang, et al.
Publicado: (2017)

A Prediction Model of the Concrete Cracking Induced by the Non-Uniform Corrosion of the Steel Reinforcement
por: ZHU, Wenjun, et al.
Publicado: (2020)

Applicability of Diffuse Ultrasound to Evaluation of the Water Permeability and Chloride Ion Penetrability of Cracked Concrete
por: Ahn, Eunjong, et al.
Publicado: (2018)

Corrosion Resistance of Concrete Reinforced by Zinc Phosphate Pretreated Steel Fiber in the Presence of Chloride Ions
por: Zhao, Xingke, et al.
Publicado: (2020)

Assessment of the Corrosion of Steel Embedded in an Alkali-Activated Hybrid Concrete Exposed to Chlorides
por: Valencia-Saavedra, William, et al.
Publicado: (2022)

Influence of the Chloride Attack on the Post-Cracking Behavior of Recycled Steel Fiber Reinforced Concrete
por: Frazão, Cristina, et al.
Publicado: (2021)

Feasibility of Distributed Fiber Optic Sensor for Corrosion Monitoring of Steel Bars in Reinforced Concrete
por: Fan, Liang, et al.
Publicado: (2018)

Corrosion Behavior of Steel Reinforcement in Concrete with Recycled Aggregates, Fly Ash and Spent Cracking Catalyst
por: Gurdián, Hebé, et al.
Publicado: (2014)

Steel Corrosion Evaluation of Basalt Fiber RPC Affected by Crack and Steel-Concrete Interface Damage Using Electrochemical Methods
por: Liu, Hanbing, et al.
Publicado: (2020)

Corrosion of steel in concrete : prevention, diagnosis, repair /
Publicado: (2004)

Chloride Diffusion in Concrete Protected with a Silane-Based Corrosion Inhibitor
por: Coppola, Luigi, et al.
Publicado: (2020)

Corrosion Assessment of Steel Bars Used in Reinforced Concrete Structures by Means of Eddy Current Testing
por: de Alcantara, Naasson P., et al.
Publicado: (2015)

Use of Non-Linear Ultrasonic Techniques to Detect Cracks Due to Steel Corrosion in Reinforced Concrete Structures
por: Climent, Miguel Ángel, et al.
Publicado: (2019)

Analysis of the Effect of Protective Properties of Concretes with Similar Composition on the Corrosion Rate of Reinforcing Steel Induced by Chloride Ions
por: Szweda, Zofia, et al.
Publicado: (2023)

Ammonium Phosphate as Inhibitor to Mitigate the Corrosion of Steel Rebar in Chloride Contaminated Concrete Pore Solution
por: Mandal, Soumen, et al.
Publicado: (2020)

The Depth–Width Correlation for Shrinkage-Induced Cracks and Its Influence on Chloride Diffusion into Concrete
por: Zhu, Hongguang, et al.
Publicado: (2020)

Controlling chloride ions diffusion in concrete
por: Zeng, Lunwu, et al.
Publicado: (2013)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Concrete Cover Cracking and Reinforcement Corrosion Behavior in Concrete with New-to-Old Concrete Interfaces
por: Zhang, Juhui, et al.
Publicado: (2023)

Experimental Study on the Influence of Transverse Crack on Chloride Ingress in Concrete Slab Track of High-Speed Railway
por: Liu, Xiaochun, et al.
Publicado: (2023)

Corrosion behavior of HRB400 and HRB400M steel bars in concrete under DC interference
por: Ding, Qingmiao, et al.
Publicado: (2021)

Modeling Corrosion Product Film Formation and Hydrogen Diffusion at the Crack Tip of Austenitic Stainless Steel
por: Yang, Fuqiang, et al.
Publicado: (2023)

Rebar Corrosion Investigation in Rubber Aggregate Concrete via the Chloride Electro-Accelerated Test
por: Liang, Jian, et al.
Publicado: (2019)

Effect of NaCl Solution and Simulated Concrete Pore Solution Environment on the Efficiency of Steel Bar Energized Corrosion
por: Jianyu, Yang, et al.
Publicado: (2022)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Chloride Distribution and Steel Corrosion in a Concrete Bridge after Long-Term Exposure to Natural Marine Environment
por: Liu, Jun, et al.
Publicado: (2020)

Corrosion-Effected Bond Behavior between PVA-Fiber-Reinforced Concrete and Steel Rebar under Chloride Environment
por: Zhang, Xuhui, et al.
Publicado: (2023)

Ion-triggered calcium hydroxide microcapsules for enhanced corrosion resistance of steel bars
por: Liang, Zi, et al.
Publicado: (2018)

Exploring Exact Effects of Various Factors on Chloride Diffusion in Cracked Concrete: ABAQUS-Based Mesoscale Simulations
por: Zhao, Ruiqi, et al.
Publicado: (2023)

Bearing Strength of Concrete-Filled Steel Tube Reinforced with Internal Transverse Stiffened Bars under Axial Compression
por: Li, Nan, et al.
Publicado: (2022)

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet–Dry Cycles in Chloride Environment
por: Xue, Wen, et al.
Publicado: (2018)

The Design of Concrete Beams Reinforced with GFRP Bars Based on Crack Width
por: Tu, Jianwei, et al.
Publicado: (2022)

Cannot write session to /tmp/vufind_sessions/sess_7i16f4c7hpe1tqbk9ko0mnc61b