Hydroxyl-Group Identification Using O K-Edge XAFS in Porous Glass Fabricated by Hydrothermal Reaction and Low-Temperature Foaming

Porous glass was prepared by the hydrothermal reaction of sodium borosilicate glass, and oxygen-ion characterization was used to identify the hydroxyl groups in its surface area. A substantial amount of “water” was introduced into the ionic structure as either OH(−) groups or H(2)O molecules through...

Descripción completa

Detalles Bibliográficos
Autores principales: Suzuki, Masanori, Maruyama, Shigehiro, Umesaki, Norimasa, Tanaka, Toshihiro
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2019
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6803955/
https://www.ncbi.nlm.nih.gov/pubmed/31561457
http://dx.doi.org/10.3390/molecules24193488
Descripción
Sumario:Porous glass was prepared by the hydrothermal reaction of sodium borosilicate glass, and oxygen-ion characterization was used to identify the hydroxyl groups in its surface area. A substantial amount of “water” was introduced into the ionic structure as either OH(−) groups or H(2)O molecules through the hydrothermal reaction. When the hydrothermally treated glass was reheated at normal pressures, a porous structure was formed due to the low-temperature foaming resulting from the evaporation of H(2)O molecules and softening of the glass. Although it was expected that the OH(−) groups would remain in the porous glass, their distribution required clarification. Oxygen K-edge X-ray absorption fine structure (XAFS) spectroscopy enables the bonding states of oxygen ions in the surface area and interior to be characterized using the electron yield (EY) and fluorescence yield (FY) mode, respectively. The presence of OH(−) groups was detected in the O K-edge XAFS spectrum of the porous glass prepared by hydrothermal reaction with a corresponding pre-edge peak energy of 533.1 eV. In addition, comparison of the XAFS spectra obtained in the EY and FY modes revealed that the OH(−) groups were mainly distributed in the surface area (depths of several tens of nanometers).