Adsorption-Induced Expansion of Graphene Oxide Frameworks: Observation by in Situ Neutron Diffraction

[Image: see text] We have investigated adsorption-induced deformation in graphene oxide framework materials (GOFs) using neutron diffraction at sample pressures up to 140 bar. GOFs, made by the solvothermal reaction of graphite oxide and benzene-1,4-diboronic acid, are a suitable candidate for deformation studies due to their narrow (∼1 nm), monodispersed, slit-shaped pores whose width can be measured by diffraction techniques. We have observed, in situ, a monotonic expansion of the slit width with increasing pressure upon adsorption of xenon, methane, and hydrogen under supercritical conditions. The expansion of ∼4% observed for xenon at a pressure of 48 bar is the largest deformation yet reported for supercritical adsorption on a carbonaceous material. We find that the expansion of the three gases can be mapped onto a common curve based solely on their Lennard-Jones parameters, in a manner similar to a law of corresponding states.