Unraveling the Role of Interfaces on the Spall Failure of Cu/Ta Multilayered Systems
Molecular dynamics (MD) simulations are carried out to investigate the effects of the type and spacing of FCC/BCC interfaces on the deformation and spall behavior. The simulations are carried out using model Cu/Ta multilayers with six different types of interfaces. The results suggest that interface...
Autores principales: | Chen, Jie, Mathaudhu, Suveen N., Thadhani, Naresh, Dongare, Avinash M. |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Nature Publishing Group UK
2020
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC6959279/ https://www.ncbi.nlm.nih.gov/pubmed/31937793 http://dx.doi.org/10.1038/s41598-019-57048-9 |
Ejemplares similares
-
Interface microstructure effects on dynamic failure behavior of layered Cu/Ta microstructures
por: Kumar, Rajesh, et al.
Publicado: (2023) -
The Quasi-Coarse-Grained Dynamics Method to Unravel the Mesoscale Evolution of Defects/Damage during Shock Loading and Spall Failure of Polycrystalline Al Microstructures
por: Agarwal, Garvit, et al.
Publicado: (2017) -
Thermal and Radiation Stability in Nanocrystalline Cu
por: Thomas, Marie, et al.
Publicado: (2023) -
Spall fracture
por: Antoun, Tarabay, et al.
Publicado: (2003) -
Analysis of the coal seam spalling–failure mechanism based on the seepage instability theory
por: Qin, Hengjie, et al.
Publicado: (2019)