Effect of Er on Microstructure and Mechanical Properties of 5052 Aluminum Alloy with Big Width-To-Thickness Ratio

The effect of Er on microstructure and mechanical properties of the 5052 aluminum alloy with a big width-to-thickness ratio was investigated by a metallurgical microscope, scanning electron microscope and tensile testing machine. The results showed that the precipitates were slightly refined after Er addition and Al(3)Fe was transformed into Al(6)Fe and AlEr with/without a small amount of Fe or Si. The effect of Er on grain refinement was related to its content. When Er content was lower or higher than 0.4%, the grain would coarsen. Homogenization could refine the grain by controlling Er content and distribution in the Al matrix. Long time homogenization at high temperature would significantly reduce the strength of the 5052 aluminum alloy and 5052 aluminum alloys with low Er content, but help to improve the plasticity of those with high Er content. The ultimate tensile strength, yield strength and elongation of the as-cast 5052 aluminum alloy were 197 MPa, 117 MPa and 22.5% respectively. The strength was the highest, when Er content was 0.4 wt. % and the elongation was the best at 0.1 wt. % Er content.