Revisiting the Na(2/3)Ni(1/3)Mn(2/3)O(2) Cathode: Oxygen Redox Chemistry and Oxygen Release Suppression
[Image: see text] Sodium layered transition metal oxides have been considered as promising cathode materials for sodium ion batteries due to their large capacity and high operating voltage. However, mechanism investigations of chemical evolution and capacity failure at high voltage are inadequate. A...
Autores principales: | Zhang, Yi, Wu, Miaomiao, Ma, Jiwei, Wei, Guangfeng, Ling, Yun, Zhang, Renyuan, Huang, Yunhui |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
American Chemical Society
2020
|
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7047265/ https://www.ncbi.nlm.nih.gov/pubmed/32123741 http://dx.doi.org/10.1021/acscentsci.9b01166 |
Ejemplares similares
-
Oxygen Anion Redox Chemistry Correlated with Spin State in Ni‐Rich Layered Cathodes
por: Lu, Zhihua, et al.
Publicado: (2023) -
Air-Stable Na(x)TMO(2) Cathodes for Sodium Storage
por: Zhang, Yi, et al.
Publicado: (2019) -
Nonpolarizing oxygen-redox capacity without O-O dimerization in Na(2)Mn(3)O(7)
por: Tsuchimoto, Akihisa, et al.
Publicado: (2021) -
Mn(x+) Substitution to Improve Na(3)V(2)(PO(4))(2)F(3)-Based Electrodes for Sodium-Ion Battery Cathode
por: Su, Renyuan, et al.
Publicado: (2023) -
Excimer Laser-Deposited Na(2/3)Ni(1/4)Mn(3/4)O(2) Film Cathode for Stable Sodium-Ion Battery
por: Lin, Bailin, et al.
Publicado: (2022)