Thermogravimetric analysis and kinetic study on pyrolysis of representative medical waste composition

To obtain detailed information on the pyrolysis characteristics, a thermogravimetric study on the pyrolysis of 14 typical medical waste compositions was carried out in thermogravimetric analysis (TGA) equipment using dynamic techniques in a stream of N(2). An index representing pyrolysis reactivity of waste was presented. Kinetic parameters were obtained by Coats–Redfern method and used to model the TG curve. The results showed that: (a) Plastic, protein, cellulosic material, synthetic fibre, and rubber entered pyrolysis process in succession. (b) There was one decomposition stage in the pyrolysis of one-off medical glove, operating glove, cellulosic waste, absorbable catgut suture and adhesive plaster, while other components had two obvious weight loss stages. (c) The obtained apparent activation energy for second stage pyrolysis was comparably higher than that for first stage. (d) Each stage was controlled by only one kinetic mechanism, in which kinetic parameters were constant. (e) The degradation kinetics of medical waste may be affected by special physical and chemical treatment in the product manufacturing process. (f) Among 13 waste samples, the pyrolysis index of cellulosic matter was the highest, which indicated cellulosic matter had strong pyrolysis reactivity. (g) With increasing heating rate, TG curve and DTG peak shifted to high temperatures and main reaction interval of the sample became longer.