Preparation and Characterization of DOPO-Functionalized MWCNT and Its High Flame-Retardant Performance in Epoxy Nanocomposites

In this work, functionalized multi-walled carbon nanotubes (MWCNT) were synthesized by the reaction between acylated MWCNT and 10-(2,5-dihydroxyphenyl)-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (ODOPB). The obtained MWCNT-ODOPB was well dispersed into epoxy resins together with aluminum die...

Descripción completa

Detalles Bibliográficos
Autores principales: Gu, Liqiang, Qiu, Chen, Qiu, Jianhui, Yao, Youwei, Sakai, Eiichi, Yang, Liting
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2020
Materias:
Article
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7182840/
https://www.ncbi.nlm.nih.gov/pubmed/32156085
http://dx.doi.org/10.3390/polym12030613
Descripción
Sumario:In this work, functionalized multi-walled carbon nanotubes (MWCNT) were synthesized by the reaction between acylated MWCNT and 10-(2,5-dihydroxyphenyl)-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (ODOPB). The obtained MWCNT-ODOPB was well dispersed into epoxy resins together with aluminum diethylphosphinate (AlPi) to form flame-retardant nanocomposites. The epoxy resin nanocomposite with phosphorus content of 1.00 wt % met UL 94 V-0 rating, exhibited LOI value of 39.5, and had a higher T(g) compared to neat epoxy resin, which indicates its excellent flame retardant performance. These experimental results indicated that MWCNT-ODOPB was a compatible and efficient flame retardant for epoxy resins. Moreover, cone calorimeter analysis showed that the peak heat release rate (pHRR), total heat release (THR) values, and CO(2) production profiles of the composites decreased with an increase in the additional amount of phosphorus.

Ejemplares similares