Preparation, Characterization of Propargyl Terminal Polybutadiene and Its Crosslinked Elastomers Properties

Propargyl terminal Polybutadiene (PTPB) was successfully prepared through hydroxyl terminal polybutadiene (HTPB) end-capping modification. The FTIR and (13)C NMR results indicated that the HTPB terminal hydroxyl was thoroughly replaced and yielded the target product, PTPB, with a theoretical propargyl content of 0.66 mmol g(−1). In comparison with HTPB, PTPB has a lower viscosity. Using 1,6-diazide hexane as a curing agent, polytriazole crosslinked polybutadiene (PT(ri)PB) elastomers with various functional molar ratios (R) were prepared by CuAAC reaction, and the glass transition temperatures of the resultant PT(ri)PB elastomers were approximately −75 °C, measured by differential scanning calorimetry (DSC), nearly independent of elastomer R values. Mechanical tests indicated, that with the increase in R, the mechanical properties of PT(ri)PB elastomers exhibit a parabolic dependence on R. In addition, the thermal stability of PT(ri)PB elastomers were also studied. The findings revealed some fundamental features of polytriazole crosslinking elastomer prepared by CuAAC reaction.