Hydrogen Concentration Distribution in 2.25Cr-1Mo-0.25V Steel under the Electrochemical Hydrogen Charging and Its Influence on the Mechanical Properties
The deterioration of the mechanical properties of metal induced by hydrogen absorption threatens the safety of the equipment serviced in hydrogen environments. In this study, the hydrogen concentration distribution in 2.25Cr-1Mo-0.25V steel after hydrogen charging was analyzed following the hydrogen...
Autores principales: | Yin, Changdong, Chen, Jianjun, Ye, Dongdong, Xu, Zhou, Ge, Jiahao, Zhou, Haiting |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2020
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7288120/ https://www.ncbi.nlm.nih.gov/pubmed/32422989 http://dx.doi.org/10.3390/ma13102263 |
Ejemplares similares
-
Investigation of the Influence of Pre-Charged Hydrogen on Fracture Toughness of As-Received 2.25Cr1Mo0.25V Steel and Weld
por: Song, Yan, et al.
Publicado: (2018) -
Effect of Cementite on the Hydrogen Diffusion/Trap Characteristics of 2.25Cr-1Mo-0.25V Steel with and without Annealing
por: Song, Yan, et al.
Publicado: (2018) -
Experimental Investigation of the Effect of Hydrogen on Fracture Toughness of 2.25Cr-1Mo-0.25V Steel and Welds after Annealing
por: Song, Yan, et al.
Publicado: (2018) -
Experimental Investigation of Fatigue Crack Growth Behavior of the 2.25Cr1Mo0.25V Steel Welded Joint Used in Hydrogenation Reactors
por: Song, Yan, et al.
Publicado: (2021) -
Kinetic Analysis of High-Temperature Plastic Flow in 2.25Cr-1Mo-0.25V Steel
por: Zhang, Yongtao, et al.
Publicado: (2019)