Hybrid-abutment-restoration: effect of material type on torque maintenance and fracture resistance after thermal aging

PURPOSE: To evaluate the tightening torque maintenance with zirconia, lithium disilicate, and polyetheretherketone (PEEK) hybrid-abutment-crowns after thermal aging, in addition to assess the fracture resistance of hybrid-abutment-crowns fabricated with different materials. MATERIALS AND METHODS: Th...

Descripción completa

Detalles Bibliográficos
Autores principales:	Al-Zordk, Walid, Elmisery, Ahmed, Ghazy, Mohamed
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Springer Berlin Heidelberg 2020
Materias:	Research
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7311558/ https://www.ncbi.nlm.nih.gov/pubmed/32578068 http://dx.doi.org/10.1186/s40729-020-00220-y

Ejemplares similares

Fracture Resistance and Failure Mode of Mandibular Molar Restored by Occlusal Veneer: Effect of Material Type and Dental Bonding Surface
por: Al-Zordk, Walid, et al.
Publicado: (2021)

Resistance to Fracture of Zirconia Abutments with Different Angulations: Impact of Implant Platform Diameter
por: Saker, Samah, et al.
Publicado: (2020)

Retention strength of monolithic zirconia crowns cemented with different primer-cement systems
por: Shokry, Mohamed, et al.
Publicado: (2022)

Does Preheating Resin Cements Affect Fracture Resistance of Lithium Disilicate and Zirconia Restorations?
por: Sakrana, Amal Abdelsamad, et al.
Publicado: (2021)

Effect of restoration technique on resistance to fracture of endodontically treated anterior teeth with flared root canals
por: Borzangy, Sary S, et al.
Publicado: (2019)

Clinical and radiographic prospective study of customized one-piece titanium and one-piece fusion-sputtered zirconia implants: five-year mean follow-up
por: Hassouna, Mahy, et al.
Publicado: (2022)

PRELOAD AND TORQUE REMOVAL EVALUATION OF THREE DIFFERENT ABUTMENT SCREWS FOR SINGLE STANDING IMPLANT RESTORATIONS
por: Stüker, Rafael Augusto, et al.
Publicado: (2008)

Influence of Restorative Material on the Distribution of Loads to the Bone in Hybrid Abutment Crowns—In Vitro Study
por: Martins, Rafael Garcia, et al.
Publicado: (2023)

Implant-abutment screw removal torque values between customized titanium abutment, straight titanium abutment, and hybrid zirconia abutment after a million cyclic loading: an in vitro comparative study
por: Klongbunjit, Disayut, et al.
Publicado: (2021)

Influence of Implant Connection, Abutment Design and Screw Insertion Torque on Implant-Abutment Misfit
por: Vélez, Jorge, et al.
Publicado: (2020)

Retention of hybrid-abutment-crowns with offset implant placement: influence of Crown materials and Ti-base height
por: Alseddiek, Ahmed, et al.
Publicado: (2023)

Effect of Implant Platform Connection and Abutment Material on Removal Torque and Implant Hexagon Plastic Deformation
por: Pereira, Paulo Henrique de Souza, et al.
Publicado: (2019)

Prospective evaluation of implants‐supported, tooth‐implant supported, and teeth‐supported 3‐unit posterior monolithic zirconia fixed restorations: Bite force and patient satisfaction
por: Altayyar, Sadeq, et al.
Publicado: (2023)

The effect of repeated torque tightening on total lengths of implant abutments in different internal implant‒abutment connections
por: Saleh Saber, Fariba, et al.
Publicado: (2017)

Implant abutment using hand drivers versus torque wrench
por: Singh, Himani, et al.
Publicado: (2023)

Static and Fatigue Mechanical Performance of Abutments Materials for Dental Restorations
por: Bruno, Luigi, et al.
Publicado: (2023)

Comparison of fit accuracy and torque maintenance of zirconia and titanium abutments for internal tri-channel and external-hex implant connections
por: Siadat, Hakimeh, et al.
Publicado: (2017)

In Vitro Evaluation of Manual Torque Values Applied to Implant-Abutment Complex by Different Clinicians and Abutment Screw Loosening
por: Dincer Kose, Onur, et al.
Publicado: (2017)

2. Invitro evaluation of microlekage at implant abutment interface of titanium and zirconia abutments under different torquing forces
por: Nayak, Aishwarya
Publicado: (2018)

Micro-leakage at the implant-abutment interface with different tightening torques in vitro
por: da SILVA-NETO, João Paulo, et al.
Publicado: (2012)

Fracture resistance of monolithic translucent zirconia crown bonded with different self-adhesive resin cement: influence of MDP-containing zirconia primer after aging
por: Tyor, Shaima, et al.
Publicado: (2023)

Effects of Aging Torque Controllers on Screw Tightening Force and Bacterial Micro-Leakage on the Implant-Abutment Complex
por: Jiries, Yousef, et al.
Publicado: (2022)

Tightening torque of implant abutment using hand drivers against torque wrench and its effect on the internal surface of implant
por: Sameera, Y., et al.
Publicado: (2020)

Vertical Discrepancy in Height of Morse Cone Abutments Submitted to Different Torque Forces
por: Cordeiro, Bruno Q. S., et al.
Publicado: (2021)

Microleakage and Bacterial Adhesion with Three Restorative Materials Used to Seal Screw-access Channels of Implant Abutments: An In vitro Study
por: AlQarawi, Firas Khalid, et al.
Publicado: (2021)

An In Vitro Study of Fluid Contaminations Influences on Reverse Torque Values of Implant-Abutment Connections
por: Yang, Shuying, et al.
Publicado: (2022)

Fracture Load of CAD/CAM Feldspathic Crowns Influenced by Abutment Material
por: Bencun, Mladen, et al.
Publicado: (2020)

Stress analysis in implant, abutment, and peripheral bone with different restorative crown and abutment materials: A three-dimensional finite element analysis study
por: Rani, Sapna, et al.
Publicado: (2023)

Screw loosening and changes in removal torque relative to abutment screw length in a dental implant with external abutment connection after oblique cyclic loading
por: Lee, Joo-Hee, et al.
Publicado: (2018)

Effect of abutment screw length and cyclic loading on removal torque in external and internal hex implants
por: Mohammed, Hnd Hadi, et al.
Publicado: (2016)

Enhancing current-induced torques by abutting additional spin polarizer layer to nonmagnetic metal layer
por: Go, Gyungchoon, et al.
Publicado: (2017)

Evaluation of reverse torque values and failure loads of three different abutment designs with internal connections
por: Nokar, Saied, et al.
Publicado: (2020)

Effect of fluid contamination on reverse torque values in implant-abutment connections under oral conditions
por: Mostafavi, Azam Sadat, et al.
Publicado: (2021)

Influence of zirconia/glass veneer thickness and implant abutment material on the final shade of implant restorations
por: Woo, Manita, et al.
Publicado: (2022)

Removal capability, implant-abutment connection damage and thermal effect using ultrasonic and drilling techniques for the extraction of fractured abutment screws: an in vitro study
por: Bufalá Pérez, María, et al.
Publicado: (2022)

Loosening torque of Universal Abutment screws after cyclic loading: influence of tightening technique and screw coating
por: Bacchi, Atais, et al.
Publicado: (2015)

Reverse torque evaluation in indexed and nonindexed abutments of Morse Taper implants in a mechanical fatigue test
por: Martins, Caio Marques, et al.
Publicado: (2019)

Reverse Torque Value of Angulated Screw Channel Abutment before and after Cyclic Loading: An In Vitro Study
por: Chen, Yu-Hsuan, et al.
Publicado: (2023)

Comparison of reverse torque values of abutment screws with the application of oil-based and water-based antibacterial agents
por: Nourizadeh, Amin, et al.
Publicado: (2022)

Laboratory Fracture Resilience of Hybrid Abutments Used in Oral Rehabilitation: A Systematic Review
por: Favasuli, Luca, et al.
Publicado: (2022)

Cannot write session to /tmp/vufind_sessions/sess_qml3ru9o10r424hdpdofuqti1u