Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt
The effects of ionizing radiation on materials often reduce to “bad news”. Radiation damage usually leads to detrimental effects such as embrittlement, accelerated creep, phase instability, and radiation-altered corrosion. Here we report that proton irradiation decelerates intergranular corrosion of...
Autores principales: | Zhou, Weiyue, Yang, Yang, Zheng, Guiqiu, Woller, Kevin B., Stahle, Peter W., Minor, Andrew M., Short, Michael P. |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
Nature Publishing Group UK
2020
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7347530/ https://www.ncbi.nlm.nih.gov/pubmed/32647205 http://dx.doi.org/10.1038/s41467-020-17244-y |
Ejemplares similares
-
Behavior of Ni20Cr Alloy in Molten Nitrate Salts
por: Gomez-Guzman, Nestor Belisario, et al.
Publicado: (2022) -
Corrosion and Thermal Stability of CrMnFeNi High Entropy Alloy in Molten FLiBe Salt
por: Elbakhshwan, Mohamed, et al.
Publicado: (2019) -
Hot Corrosion Behavior of TWAS and HVOF NiCr-Based Coatings in Molten Salt
por: Lencová, Kateřina, et al.
Publicado: (2023) -
Evolution of micro-pores in Ni–Cr alloys via molten salt dealloying
por: Yu, Lin-Chieh, et al.
Publicado: (2022) -
Mitigating the susceptibility to intergranular corrosion of alloy 625 by friction-stir welding
por: Lemos, Guilherme Vieira Braga, et al.
Publicado: (2022)