Magnetically Aligned and Enriched Pathways of Zeolitic Imidazolate Framework 8 in Matrimid Mixed Matrix Membranes for Enhanced CO(2) Permeability

Metal-organic frameworks (MOFs) as additives in mixed matrix membranes (MMMs) for gas separation have gained significant attention over the past decades. Many design parameters have been investigated for MOF based MMMs, but the spatial distribution of the MOF throughout MMMs lacks investigation. The...

Descripción completa

Detalles Bibliográficos
Autores principales: van Essen, Machiel, Montrée, Esther, Houben, Menno, Borneman, Zandrie, Nijmeijer, Kitty
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2020
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7408041/
https://www.ncbi.nlm.nih.gov/pubmed/32709108
http://dx.doi.org/10.3390/membranes10070155
Descripción
Sumario:Metal-organic frameworks (MOFs) as additives in mixed matrix membranes (MMMs) for gas separation have gained significant attention over the past decades. Many design parameters have been investigated for MOF based MMMs, but the spatial distribution of the MOF throughout MMMs lacks investigation. Therefore, magnetically aligned and enriched pathways of zeolitic imidazolate framework 8 (ZIF−8) in Matrimid MMMs were synthesized and investigated by means of their N(2) and CO(2) permeability. Magnetic ZIF−8 (m–ZIF−8) was synthesized by incorporating Fe(3)O(4) in the ZIF−8 structure. The presence of Fe(3)O(4) in m–ZIF−8 showed a decrease in surface area and N(2) and CO(2) uptake, with respect to pure ZIF−8. Alignment of m–ZIF−8 in Matrimid showed the presence of enriched pathways of m–ZIF−8 through the MMMs. At 10 wt.% m–ZIF−8 incorporation, no effect of alignment was observed for the N(2) and CO(2) permeability, which was ascribed anon-ideal tortuous alignment. However, alignment of 20 wt.% m–ZIF−8 in Matrimid showed to increase the CO(2) diffusivity and permeability (19%) at 7 bar, while no loss in ideal selectivity was observed, with respect to homogeneously dispersed m–ZIF−8 membranes. Thus, the alignment of MOF particles throughout the matrix was shown to enhance the CO(2) permeability at a certain weight content of MOF.