Influence of Crack Width on Chloride Penetration in Concrete Subjected to Alternating Wetting–Drying Cycles

To investigate the durability of reinforced concrete (RC) beams under the combined actions of transverse cracks and corrosion, corrosion tests were conducted on a total of eight RC beams with different water–cement ratios and cracking states. The effects of the transverse crack width, water–cement r...

Descripción completa

Detalles Bibliográficos
Autores principales:	Lai, Jun, Cai, Jian, Chen, Qing-Jun, He, An, Wei, Mu-Yang
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2020
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7503623/ https://www.ncbi.nlm.nih.gov/pubmed/32872137 http://dx.doi.org/10.3390/ma13173801

Ejemplares similares

Chloride Penetration of Recycled Fine Aggregate Concrete under Drying–Wetting Cycles
por: Chen, Chunhong, et al.
Publicado: (2023)

Multidimensional Transport Experiment and Simulation of Chloride Ions in Concrete Subject to Simulated Dry and Wet Cycles in a Marine Environment
por: Xu, Hao, et al.
Publicado: (2023)

The Depth–Width Correlation for Shrinkage-Induced Cracks and Its Influence on Chloride Diffusion into Concrete
por: Zhu, Hongguang, et al.
Publicado: (2020)

Mechanical Performance of Steel Fibre Reinforced Concrete Exposed to Wet–Dry Cycles of Chlorides and Carbon Dioxide
por: Marcos-Meson, Victor, et al.
Publicado: (2021)

Applicability of Diffuse Ultrasound to Evaluation of the Water Permeability and Chloride Ion Penetrability of Cracked Concrete
por: Ahn, Eunjong, et al.
Publicado: (2018)

Damage Evolution of Polypropylene–Basalt Hybrid Fiber Ceramsite Concrete under Chloride Erosion and Dry–Wet Cycle
por: Zhu, Hongbing, et al.
Publicado: (2023)

Investigation of the Mechanical Properties of Iron Tailings Concrete Subjected to Dry–Wet Cycle and Negative Temperature
por: Liu, Xiaozhou, et al.
Publicado: (2023)

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet–Dry Cycles in Chloride Environment
por: Xue, Wen, et al.
Publicado: (2018)

Protective Performance of Coated Reinforcement in Coral Concrete under Dry/Wet Cycling
por: Cao, Hongji, et al.
Publicado: (2023)

Chloride Diffusion Property of Hybrid Basalt–Polypropylene Fibre-Reinforced Concrete in a Chloride–Sulphate Composite Environment under Drying–Wetting Cycles
por: Luo, Yang, et al.
Publicado: (2021)

Effect of Carbonation on Chloride Maximum Phenomena of Concrete Subjected to Cyclic Wetting–Drying Conditions: A Numerical and Experimental Study
por: Xu, Lina, et al.
Publicado: (2022)

Analysis of Crack Width Development in Reinforced Concrete Beams
por: Goszczyńska, Barbara, et al.
Publicado: (2021)

Assessment of Cracking Widths in a Concrete Wall Based on TIR Radiances of Cracking
por: Su, Tung-Ching
Publicado: (2020)

Study on the Deterioration of Concrete under Dry–Wet Cycle and Sulfate Attack
por: Liu, Fang, et al.
Publicado: (2020)

Influence of Wetting and Drying Cycles on Physical and Mechanical Behavior of Recycled Aggregate Concrete
por: Rangel, Caroline S., et al.
Publicado: (2020)

The Design of Concrete Beams Reinforced with GFRP Bars Based on Crack Width
por: Tu, Jianwei, et al.
Publicado: (2022)

Pure shear model for crack width analysis of reinforced concrete members
por: Sakalauskas, Karolis, et al.
Publicado: (2023)

Reliability Analysis of Bond Behaviour of CFRP–Concrete Interface under Wet–Dry Cycles
por: Liang, Hongjun, et al.
Publicado: (2018)

Mechanical Properties, Crack Width, and Propagation of Waste Ceramic Concrete Subjected to Elevated Temperatures: A Comprehensive Study
por: Najm, Hadee Mohammed, et al.
Publicado: (2022)

Effect of Dry–Wet Ratio on Properties of Concrete Under Sulfate Attack
por: Guo, Jin-Jun, et al.
Publicado: (2019)

Application of Ag/AgCl Sensor for Chloride Monitoring of Mortar under Dry-Wet Cycles
por: Tian, Yupeng, et al.
Publicado: (2020)

Prediction of Crack Width in RC Piles Exposed to Local Corrosion in Chloride Environment
por: Shao, Wei, et al.
Publicado: (2023)

Modelling of Corrosion-Induced Concrete Cover Cracking Due to Chloride Attacking
por: Lun, Pei-Yuan, et al.
Publicado: (2021)

Novel Nano-Precursor Inhibiting Material for Improving Chloride Penetration Resistance of Concrete: Evaluation and Mechanism
por: Chen, Ruixing, et al.
Publicado: (2021)

Chloride Transport Behaviour and Service Performance of Cracked Concrete Linings in Coastal Subway Tunnels
por: Zhang, Sulei, et al.
Publicado: (2021)

Quantification of the Influence of Concrete Width per Fiber Strand on the Splitting Crack Failure of Textile Reinforced Concrete (TRC)
por: Beßling, Markus, et al.
Publicado: (2022)

Strength deterioration prediction of pervious concrete in sulfate and dry-wet cycle environments utilizing ultrasonic velocity
por: Song, Hui, et al.
Publicado: (2023)

Drying Shrinkage and Rapid Chloride Penetration Resistance of Recycled Aggregate Concretes Using Cement Paste Dissociation Agent
por: Yang, Sungchul, et al.
Publicado: (2021)

Time and Crack Width Dependent Model of Chloride Transportation in Engineered Cementitious Composites (ECC)
por: Bu, Linglai, et al.
Publicado: (2022)

Study on Crack Development and Micro-Pore Mechanism of Expansive Soil Improved by Coal Gangue under Drying–Wetting Cycles
por: Zhu, Hongxing, et al.
Publicado: (2021)

Experimental Study on Mechanical Properties of High-Ductility Concrete against Combined Sulfate Attack and Dry–Wet Cycles
por: Li, Lingling, et al.
Publicado: (2021)

Influence of the Chloride Attack on the Post-Cracking Behavior of Recycled Steel Fiber Reinforced Concrete
por: Frazão, Cristina, et al.
Publicado: (2021)

Recovery of Chloride Penetration Resistance of Cement-Based Composites Due to Self-Healing of Cracks
por: Yoo, Kyung Suk, et al.
Publicado: (2021)

Deterioration characteristics of cement-improved loess under dry–wet and freeze–thaw cycles
por: Jiang, Ying-jun, et al.
Publicado: (2021)

Experimental Investigation on the Influence of Crack Width of Asphalt Concrete on the Repair Effect of Microbially Induced Calcite Precipitation
por: Fan, Ling, et al.
Publicado: (2023)

Macrocell Corrosion of Steel in Concrete under Carbonation, Internal Chloride Admixing and Accelerated Chloride Penetration Conditions
por: Jiang, Zhilu, et al.
Publicado: (2021)

Permeability characteristics and structural evolution of compacted loess under different dry densities and wetting-drying cycles
por: Yuan, Kang-ze, et al.
Publicado: (2021)

Experimental Study on the Variation of Surface Widths of Lignite Desiccation Cracks during Low-Temperature Drying
por: Dong, Ziwen, et al.
Publicado: (2021)

Probabilistic Modeling of Chloride Penetration with Respect to Concrete Heterogeneity and Epoxy-Coating on the Reinforcement
por: Le, Tuan Duc, et al.
Publicado: (2019)

A Review on the Carbonation and Chloride Penetration Resistance of Structural Lightweight Aggregate Concrete
por: Bogas, José Alexandre, et al.
Publicado: (2019)

Cannot write session to /tmp/vufind_sessions/sess_v00lue8i5utjse7dkgauv8a4ni