Influence of Laser Powder Bed Fusion Process Parameters on Voids, Cracks, and Microhardness of Nickel-Based Superalloy Alloy 247LC
The manufacturing of parts from nickel-based superalloy Alloy 247LC by laser powder bed fusion (L-PBF) is challenging, primarily owing to the alloy’s susceptibility to cracks. Apart from the cracks, voids created during the L-PBF process should also be minimized to produce dense parts. In this study...
Autores principales: | Adegoke, Olutayo, Andersson, Joel, Brodin, Håkan, Pederson, Robert |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2020
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7503919/ https://www.ncbi.nlm.nih.gov/pubmed/32859031 http://dx.doi.org/10.3390/ma13173770 |
Ejemplares similares
-
Fabrication of Crack-Free Nickel-Based Superalloy Considered Non-Weldable during Laser Powder Bed Fusion
por: Sanchez-Mata, Oscar, et al.
Publicado: (2018) -
A Novel γ′-Strengthened Nickel-Based Superalloy for Laser Powder Bed Fusion
por: Xu, Jinghao, et al.
Publicado: (2020) -
2-D Selector Simulation Studies on Grain Selection for Single Crystal Superalloy of CM247LC
por: Zhang, Hang, et al.
Publicado: (2019) -
Thermal Barrier Stability and Wear Behavior of CVD Deposited Aluminide Coatings for MAR 247 Nickel Superalloy
por: Kukla, Dominik, et al.
Publicado: (2020) -
Powder Interlayer Bonding of Nickel-Based Superalloys with Dissimilar Chemistries
por: Stanners, Olivia, et al.
Publicado: (2021)