Comparative evaluation of push-out bond strength of gutta-percha using different sealers with lateral condensation and thermoplasticized obturation technique: An in vitro study

AIM: The study aimed to evaluate and compare the push-out bond strength of gutta-percha using AH plus, Endosequence BC, and Roeko seal sealer with lateral condensation and thermoplasticized obturation technique. MATERIALS AND METHODS: Sixty single-rooted premolars were instrumented and samples were randomly assigned into three groups based on the sealer used (Group A-AH Plus, Group B-Endosequence BC, Group C-Roeko Seal) which were further divided into two subgroups-A1, B1, and C1 were obturated by the lateral condensation technique and A2, B2, and C2 using the thermoplasticized technique. Each sample was sectioned horizontally using a diamond disc, representing apical, middle, and coronal thirds, respectively. Root segments were then mounted on an acrylic block, and push-out bond strength of each sample was tested using the universal testing machine. STATISTICAL ANALYSIS: One-way ANOVA, Tukey's test, and unpaired t-test. RESULTS: For mandibular premolar teeth with a single canal using lateral condensation technique, the highest push-out bond strength was found in the A1 group (7.30 ± 0.61 MPa) at the apical level. While using the thermoplasticized technique, the highest push-out bond strength was found in the B2 group (3.71 ± 0.81 MPa) at the apical level. Overall results showed that the lateral condensation technique showed significantly higher push-out bond strength than thermoplasticized technique (P < 0.028). CONCLUSIONS: The push-out bond strength of AH Plus sealer was higher than the Endosequence BC sealer and Roeko seal sealer. Lateral condensation technique has shown higher push-out bond strength than the thermoplasticized technique.