Fabrication and Electrolyte Characterizations of Nanofiber Framework-Based Polymer Composite Membranes with Continuous Proton Conductive Pathways
For future fuel cell operations under high temperature and low- or non-humidified conditions, high-performance polymer electrolyte membranes possessing high proton conductivity at low relative humidity as well as suitable gas barrier property and sufficient membrane stability are strongly desired. I...
Autores principales: | , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2021
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7911994/ https://www.ncbi.nlm.nih.gov/pubmed/33513962 http://dx.doi.org/10.3390/membranes11020090 |
Sumario: | For future fuel cell operations under high temperature and low- or non-humidified conditions, high-performance polymer electrolyte membranes possessing high proton conductivity at low relative humidity as well as suitable gas barrier property and sufficient membrane stability are strongly desired. In this study, novel nanofiber framework (NfF)-based composite membranes composed of phytic acid (Phy)-doped polybenzimidazole nanofibers (PBINf) and Nafion matrix electrolyte were fabricated through the compression process of the nanofibers. The NfF composite membrane prepared from the pressed Phy-PBINf showed higher proton conductivity and lower activation energy than the conventional NfF composite and recast-Nafion membranes, especially at low relative humidity. It is considered that the compression process increased the nanofiber contents in the composite membrane, resulting in the construction of the continuously formed effective proton conductive pathway consisting of the densely accumulated phosphoric acid and sulfonic acid groups at the interface of the nanofibers and the Nafion matrix. Since the NfF also improved the mechanical strength and gas barrier property through the compression process, the NfF composite polymer electrolyte membranes have the potential to be applied to future fuel cells operated under low- or non-humidified conditions. |
---|