Improving Cyclability of Lithium Metal Anode via Constructing Atomic Interlamellar Ion Channel for Lithium Sulfur Battery

Uniform migration of lithium (Li) ions between the separator and the lithium anode is critical for achieving good quality Li deposition, which is of much significance for lithium metal battery operation, especially for Li–sulfur (Li–S) batteries. Commercial separators such as polypropylene or polyet...

Descripción completa

Detalles Bibliográficos
Autores principales: Yang, Mao, Jue, Nan, Chen, Yuanfu, Wang, Yong
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Springer US 2021
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7988023/
https://www.ncbi.nlm.nih.gov/pubmed/33759059
http://dx.doi.org/10.1186/s11671-021-03508-z
Descripción
Sumario:Uniform migration of lithium (Li) ions between the separator and the lithium anode is critical for achieving good quality Li deposition, which is of much significance for lithium metal battery operation, especially for Li–sulfur (Li–S) batteries. Commercial separators such as polypropylene or polyethylene can be prepared by wet or dry processes, but they can indeed cause plentiful porosities, resulting in the uneven Li ion stripping/plating and finally the formation of Li dendrites. Thence, we constructed an atomic interlamellar ion channel by introducing the layered montmorillonite on the surface of the separator to guide Li ion flux and achieved stable Li deposition. The atomic interlamellar ion channel with a spacing of 1.4 nm showed strong absorption capacity for electrolytes and reserved capacity for Li ions, thus promoting rapid transfer of Li ions and resulting in even Li ion deposition at the anode. When assembled with the proposed separator, the Coulombic efficiency of Li||Cu batteries was 98.2% after 200 cycles and stable plating/stripping even after 800 h was achieved for the Li||Li symmetric batteries. Importantly, the proposed separator allows 140% specific capacity increase after 190 cycles as employing the Li–S batteries. SUPPLEMENTARY INFORMATION: The online version contains supplementary material available at 10.1186/s11671-021-03508-z.