Electrically Conducting Pullulan-Based Nanobiocomposites Using Carbon Nanotubes and TEMPO Cellulose Nanofibril

Hybrid nanobiocomposite films are prepared using a solution casting by incorporating TEMPO cellulose nanofibrils (TOCNs) and carbon nanotubes (CNTs) into an aqueous solution of pullulan (PULL). The presence of CNT is confirmed by XRD characterization, and the prepared film shows an increased degree...

Descripción completa

Detalles Bibliográficos
Autores principales: Yeasmin, Sabina, Yeum, Jeong Hyun, Ji, Byung Chul, Choi, Jin Hyun, Yang, Seong Baek
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2021
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC7997298/
https://www.ncbi.nlm.nih.gov/pubmed/33670897
http://dx.doi.org/10.3390/nano11030602
Descripción
Sumario:Hybrid nanobiocomposite films are prepared using a solution casting by incorporating TEMPO cellulose nanofibrils (TOCNs) and carbon nanotubes (CNTs) into an aqueous solution of pullulan (PULL). The presence of CNT is confirmed by XRD characterization, and the prepared film shows an increased degree of crystallinity after the addition of TOCNs and CNT. The maximum degree of crystallinity value is obtained for CNT 0.5 % (59.64%). According to the Fourier-transform infrared spectroscopy, the shifts of the characteristic -OH peak of PULL occurred after the addition of TOCNs and aqueous CNT (3306.39 to 3246.90 cm(−1)), confirming interaction between the TOCNs, CNTs, and PULL matrix. The prepared films show enhanced material properties including higher tensile strength (65.41 MPa at low CNT content (0.5%)), water barrier properties, and reduced moisture susceptibility (5 wt.% CNT shows the lowest value (11.28%)) compared with the neat PULL film. Additionally, the prepared films are almost biodegradable within 64 days and show excellent electrical conductivity (0.001 to 0.015 S/mm for 0.5–5% CNT), which suggests a new approach to transform natural polymers into novel advanced materials for use in the fields of biosensing and electronics.