Quantification Approaches for Fatigue Crack Resistance of Thermoplastic Tape Layered Composites with Multiple Delaminations

Automated tape placement with in-situ consolidation (ATPisc) is a layer-wise manufacturing process in which the achievement of proper interlayer bonding constitutes one of the most challenging aspects. In the present study, unidirectional carbon fiber reinforced thermoplastic laminates were produced...

Descripción completa

Detalles Bibliográficos
Autores principales:	Khudiakova, Anastasiia, Brunner, Andreas J., Wolfahrt, Markus, Pinter, Gerald
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2021
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8002822/ https://www.ncbi.nlm.nih.gov/pubmed/33803010 http://dx.doi.org/10.3390/ma14061476

Ejemplares similares

Experimental and Numerical Study of Healing Effect on Delamination Defect in Infusible Thermoplastic Composite Laminates
por: Griskevicius, Paulius, et al.
Publicado: (2023)

Effect of Plasma-Treatment of Interleaved Thermoplastic Films on Delamination in Interlayer Fibre Hybrid Composite Laminates
por: Marino, Salvatore Giacomo, et al.
Publicado: (2020)

Vibration-Based In-Situ Detection and Quantification of Delamination in Composite Plates
por: Mei, Hanfei, et al.
Publicado: (2019)

On the Mode I and Mode II Delamination Characteristics and Surface Morphological Aspects of Composites with Carbon-Thermoplastic Hybrid Fabrics and Innovative Liquid Thermoplastic Resin
por: Bhudolia, Somen K., et al.
Publicado: (2022)

Layer charge robust delamination of organo-clays
por: Daab, Matthias, et al.
Publicado: (2018)

Thermoplastic Pultrusion Process of Polypropylene/Glass Tapes
por: Tucci, Fausto, et al.
Publicado: (2023)

Microwave Non-Destructive Testing for Delamination Detection in Layered Composite Pipelines
por: Sobkiewicz, Przemysław, et al.
Publicado: (2021)

The interplay of crack hopping, delamination and interface failure in drying nanoparticle films
por: Yang, Bin, et al.
Publicado: (2016)

Towards Tough Thermoplastic Adhesive Tape by Microstructuring the Tape Using Tailored Defects
por: Wagih, Ahmed, et al.
Publicado: (2023)

Delamination of Novel Carbon Fibre-Based Non-Crimp Fabric-Reinforced Thermoplastic Composites in Mode I: Experimental and Fractographic Analysis
por: Mohsin, Muhammad Ameerul Atrash, et al.
Publicado: (2023)

Delamination buckling of composite materials
por: Kachanov, L M
Publicado: (1988)

Bonding of thermoplastic microfluidics by using dry adhesive tape
por: Tsao, Chia-Wen, et al.
Publicado: (2020)

Detection and Quantification of Delamination Failures in Marine Composite Bulkheads via Vibration Energy Variations
por: Garcia, Cristobal, et al.
Publicado: (2021)

Electrothermally Self-Healing Delamination Cracks in Carbon/Epoxy Composites Using Sandwich and Tough Carbon Nanotube/Copolymer Interleaves
por: Ouyang, Qin, et al.
Publicado: (2022)

Optimizing the Process of Spot Welding of Polycarbonate-Matrix-Based Unidirectional (UD) Thermoplastic Composite Tapes
por: Birtha, Janos, et al.
Publicado: (2023)

Lay-Up and Consolidation of a Composite Pipe by In Situ Ultrasonic Welding of a Thermoplastic Matrix Composite Tape
por: Dell’Anna, Riccardo, et al.
Publicado: (2018)

Improvement of a Cohesive Zone Model for Fatigue Delamination Rate Simulation
por: Pirondi, Alessandro, et al.
Publicado: (2019)

Preliminary Study on Assessing Delaminated Cracks in Cement Asphalt Mortar Layer of High-Speed Rail Track Using Traditional and Normalized Impact–Echo Methods
por: Ke, Ying-Tzu, et al.
Publicado: (2020)

Comparison of the cohesive and delamination fatigue properties of atomic-layer-deposited alumina and titania ultrathin protective coatings deposited at 200 °C
por: Sadeghi-Tohidi, Farzad, et al.
Publicado: (2014)

Relationship Between Matrix Cracking and Delamination in CFRP Cross-Ply Laminates Subjected to Low Velocity Impact
por: Tan, Riming, et al.
Publicado: (2019)

Delamination of Layered Double Hydroxide in Ionic Liquids under Ambient Conditions
por: Takács, Dóra, et al.
Publicado: (2022)

Fretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life
por: Noraphaiphipaksa, Nitikorn, et al.
Publicado: (2017)

Detection of delamination of steel–polymer sandwich composites using acoustic emission and development of a forming limit diagram considering delamination
por: Yang, Jewook, et al.
Publicado: (2023)

Influence of the Test Method on the Characterization of the Fatigue Delamination Behavior of a Composite Material under Mixed Mode I/II Fracture
por: Argüelles, Antonio, et al.
Publicado: (2019)

Study of the fatigue delamination behaviour of adhesive joints in carbon fibre reinforced epoxy composites, influence of the period of exposure to saline environment
por: Argüelles, A., et al.
Publicado: (2022)

About the Role of Interfaces on the Fatigue Crack Propagation in Laminated Metallic Composites
por: Pohl, Philip Manuel, et al.
Publicado: (2021)

From quantum to continuum mechanics in the delamination of atomically-thin layers from substrates
por: Hauseux, Paul, et al.
Publicado: (2020)

The delamination theory of wear
por: Suh, Nam P
Publicado: (1977)

Dynamic Mechanical Analysis on Delaminated Flax Fiber Reinforced Composites
por: Shen, Yiou, et al.
Publicado: (2019)

Prediction of the Delamination at the Steel and CFRP Interface of Hybrid Composite Part
por: Park, Jun-Su, et al.
Publicado: (2021)

The Strength and Delamination of Graphene/Cu Composites with Different Cu Thicknesses
por: Kim, Song-Mi, et al.
Publicado: (2021)

Stitching Repair for Delaminated Carbon Fiber/Bismaleimide Composite Laminates
por: Hua, Jiantao, et al.
Publicado: (2022)

Study on the Influence of Delamination Damage on the Processing Quality of Composite Laminates
por: Yu, Jiali, et al.
Publicado: (2022)

Enhancing the low-level tape layer of CERN Tape Archive software
por: Moraru, Cristina Gabriela
Publicado: (2017)

Cyclic Deformation and Fatigue Failure Mechanisms of Thermoplastic Polyurethane in High Cycle Fatigue
por: Wang, Shuo, et al.
Publicado: (2023)

Research on the Fatigue Crack Growth Behavior of a Zr/Ti/Steel Composite Plate with a Crack Normal to the Interface
por: Zhou, Binbin, et al.
Publicado: (2023)

Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset
por: Jin, Huijin, et al.
Publicado: (2019)

Structure-Property Relationships of Polyamide 12 Grades Exposed to Rapid Crack Extension
por: Messiha, Mario, et al.
Publicado: (2021)

Retraction pattern of delaminated rotator cuff tears: dual-layer rotator cuff repair
por: Cha, Sang-Won, et al.
Publicado: (2016)

Arthroscopic Knotless Separate Layer Transosseous Equivalent Repair of Delaminated Rotator Cuff Tears
por: Buyukdogan, Kadir, et al.
Publicado: (2019)

Cannot write session to /tmp/vufind_sessions/sess_1gqhc1d47e5f2m4a35nf3o6kfd