Experimental data on fracture of open-hole composite laminates subjected to tension loading

In this data article, we present detailed failure process of big open-hole carbon fibre reinforced polymer (CFRP) composite laminates subjected to tension loading, which are tested by digital image correlation (DIC) system and electrical strain gauge system. In experiments, three different lay-ups a...

Descripción completa

Detalles Bibliográficos
Autores principales:	Ma, Zhaoyang, Chen, Jianlin, Li, Zheng, Su, Xianyue
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Elsevier 2021
Materias:	Data Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8010642/ https://www.ncbi.nlm.nih.gov/pubmed/33816726 http://dx.doi.org/10.1016/j.dib.2021.106876

Ejemplares similares

Dataset on open/blind hole-hole interaction in barely visible impact damaged composite laminates
por: Lai, W.L., et al.
Publicado: (2020)

Open Hole Tension of 3D Printed Aligned Discontinuous Composites
por: Krajangsawasdi, Narongkorn, et al.
Publicado: (2022)

Enhanced Open-Hole Strength and Toughness of Sandwich Carbon-Kevlar Woven Composite Laminates
por: Khan, Mohammad K. A., et al.
Publicado: (2023)

VO-Notches Subjected to Tension–Torsion Loading: Experimental and Theoretical Fracture Study on Polymeric Samples
por: Talebi, Hossein, et al.
Publicado: (2023)

CFRP Thin-Ply Fibre Metal Laminates: Influences of Ply Thickness and Metal Layers on Open Hole Tension and Compression Properties
por: Kötter, Benedikt, et al.
Publicado: (2020)

Analytical Method for the Optimization of the Open-Hole and Filled-Hole Laminates at the Preliminary Design Stage
por: Sajid, Zubair, et al.
Publicado: (2023)

Modified Micro-Mechanics Based Multiscale Model for Damage Analysis of Open-Hole Composite Laminates under Compression
por: Wang, Meng, et al.
Publicado: (2022)

Finite Element Modeling of Laminated Composite Plates with Locally Delaminated Interface Subjected to Impact Loading
por: Abo Sabah, Saddam Hussein, et al.
Publicado: (2014)

Effect of Hole Arrangement on Failure Mechanism of Multiple-Hole Fiber Metal Laminate under On-Axis and Off-Axis Loading
por: Zhang, Jipeng, et al.
Publicado: (2021)

A Fatigue Model to Predict Interlaminar Damage of FRP Composite Laminates Subjected to Mode I Load
por: Khan, Safdar Ali, et al.
Publicado: (2023)

Experimental dataset on the residual performance of fiber-reinforced cementitious composite subjected to high temperature
por: Soares Junior, Paulo Roberto Ribeiro, et al.
Publicado: (2022)

Permanent Deformation and Stiffness Degradation of Open Hole Glass/PA6 UD Thermoplastic Composite in Tension and Compression
por: Sevenois, Ruben Dirk, et al.
Publicado: (2021)

Load-displacement experimental data from axial tensile loading of CFRP-SPCC hybrid laminates
por: Muflikhun, Muhammad Akhsin, et al.
Publicado: (2020)

Experimental and Numerical Analysis of Mixed I-214 Poplar/Pinus Sylvestris Laminated Timber Subjected to Bending Loadings
por: Rescalvo, Francisco J., et al.
Publicado: (2020)

Dynamic Behavior of Laminated Magnets With Solid Tension Bars
por: Zickler, Thomas
Publicado: (2018)

Peculiarities in the Material Design of Buckling Resistance for Tensioned Laminated Composite Panels with Elliptical Cut-Outs
por: Muc, Aleksander
Publicado: (2018)

Experimental and Numerical Investigation into the Mechanical Behavior of Composite Solid Propellants Subject to Uniaxial Tension
por: Wu, Chengfeng, et al.
Publicado: (2023)

Fracture Resistance of Ceramic Laminate Veneers Bonded to Teeth with Class V Composite Fillings after Cyclic Loading
por: Sadighpour, Leyla, et al.
Publicado: (2018)

Experimental investigation of reinforced bonded joints for composite laminates
por: Bisagni, Chiara, et al.
Publicado: (2017)

Stress-strain and microscopy data for fire-damaged aluminum alloy 6061 subjected to multiaxial loading
por: Puplampu, S.B., et al.
Publicado: (2021)

Dataset for surface and internal damage after impact on CFRP laminates
por: Hasebe, Saki, et al.
Publicado: (2022)

Comparison of the Therapeutic Effects of Tension Band with Cannulated Screw and Tension Band with Kirschner Wire on Patella Fracture
por: Liu, Chengwu, et al.
Publicado: (2020)

Effect of Impact Position on Repaired Composite Laminates Subjected to Multi-Impacts
por: Reis, Paulo N. B., et al.
Publicado: (2022)

In vitro evaluation of the fracture resistance and microleakage of porcelain laminate veneers bonded to teeth with composite fillings after cyclic loading
por: Sadighpour, Leyla, et al.
Publicado: (2014)

Damage evolution and fracture behavior of different materials specimens containing a central hole subjected to local loading
por: Ji, Dongliang, et al.
Publicado: (2022)

A New Failure Theory and Importance Measurement Analysis for Multidirectional Fiber-Reinforced Composite Laminates with Holes
por: Li, Shu, et al.
Publicado: (2022)

Experimental data on open circuit voltage characterization for Li-ion batteries
por: Ahmed, Mostafa Shaban, et al.
Publicado: (2021)

Experimental and Numerical Analysis of Stitched Composite Laminates Subjected to Low-Velocity Edge-on Impact and Compression after Edge-on Impact
por: Liu, Bangxiong, et al.
Publicado: (2023)

Efficient Improvement in Fracture Toughness of Laminated Composite by Interleaving Functionalized Nanofibers
por: Razavi, Seyed Mohammad Javad, et al.
Publicado: (2021)

Dataset on mechanical properties of damaged fibre composite laminates with drilled vent-holes for resin-injection repair procedure
por: Lai, W.L., et al.
Publicado: (2019)

Effect of Strain Rate Sensitivity on Fracture of Laminated Rings under Dynamic Compressive Loading
por: Partovi, Amir, et al.
Publicado: (2022)

Nonlinear Analytical Procedure for Predicting Debonding of Laminate from Substrate Subjected to Monotonic or Cyclic Load
por: Lamberti, Marco, et al.
Publicado: (2022)

Experimental Study on Compression Failure of Composite Laminates with Prefabricated Surface Cracks
por: Sun, Wei, et al.
Publicado: (2021)

Data in experimental stand-alone microgrid: Solar production, domestic loads, battery storage and meteorological series
por: Calogine, Didier, et al.
Publicado: (2023)

Experimental data on the properties of natural fiber particle reinforced polymer composite material
por: Chandramohan, D., et al.
Publicado: (2017)

The experimental and finite element analysis data of Cu-UV glue composite materials
por: Chen, Xiaoyong, et al.
Publicado: (2021)

Coordinated increase of nuclear tension and lamin-A with matrix stiffness outcompetes lamin-B receptor that favors soft tissue phenotypes
por: Buxboim, Amnon, et al.
Publicado: (2017)

A Simplified Computational Strategy Focused on Resin Damage to Study Matrix Cracking of The Cross-Ply Laminates Under Uniaxial Tension Load
por: Sun, Liangliang, et al.
Publicado: (2019)

Natural Composite Reinforced by Lontar (Borassus flabellifer) Fiber: An Experimental Study on Open-Hole Tensile Strength
por: Bale, Jefri, et al.
Publicado: (2017)

An Experimental and Numerical Investigation to Characterize an Aerospace Composite Material with Open-Hole Using Non-Destructive Techniques
por: Feito, Norberto, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_41qveb1p3g5f2a0la7cc8vn4ll