The Effect of Graphene Nanofiller on the Surface Structure and Performance of Epoxy Resin–Polyhedral Oligomeric Silsesquioxane (EP-POSS)

Epoxy resin–polyhedral oligomeric silsesquioxane (EP-POSS) has excellent mechanical properties and hydrophobic properties. In order to adapt for application in sensor and photovoltaic fields, graphene, nano-SiO(2) and nano-ZnO were used to modify EP-POSS. FTIR was used to characterize changes on the surface structure after introducing nanoparticles. The change of hydrophobicity was measured using a contact angle test. TEM test results showed that nanoparticles were successfully inserted between the graphene sheets. However, the content of Si on the surface was low, as the cage structure of POSS in the molecular chain was coated by epoxy groups. XRD tests indicated that nanoparticles facilitated the dispersion of graphene in EP-POSS. XPS characterized the chemical state and content of the elements, confirming that the addition of graphene can induce the enrichment of Si on the surface of EP-POSS, which had a shielding effect on the main chain and improved the hydrophobicity. Wear resistance and adhesion tests showed that, after the introduction of nanoparticles, the EP-POSS coating film met the requirements of graphene materials.