Resin Composite Materials for Chairside CAD/CAM Restorations: A Comparison of Selected Mechanical Properties

OBJECTIVE: The aim was to evaluate the flexural strength, flexural modulus, microhardness, Weibull modulus, and characteristic strength of six resin composite blocks (Grandio Blocs-GR, Tetric CAD-TE, Brilliant Crios-CR, Katana Avencia-AV, Cerasmart-CS, and Shofu Block HC-HC). METHODS: Flexural stren...

Descripción completa

Detalles Bibliográficos
Autores principales: Grzebieluch, Wojciech, Mikulewicz, Marcin, Kaczmarek, Urszula
Formato: Online Artículo Texto
Lenguaje:English
Publicado: Hindawi 2021
Materias:
Research Article
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8099508/
https://www.ncbi.nlm.nih.gov/pubmed/34007429
http://dx.doi.org/10.1155/2021/8828954
Descripción
Sumario:OBJECTIVE: The aim was to evaluate the flexural strength, flexural modulus, microhardness, Weibull modulus, and characteristic strength of six resin composite blocks (Grandio Blocs-GR, Tetric CAD-TE, Brilliant Crios-CR, Katana Avencia-AV, Cerasmart-CS, and Shofu Block HC-HC). METHODS: Flexural strength and flexural modulus were measured using a three-point bending test and microhardness using the Vickers method. Weibull analysis was also performed. RESULTS: The materials showed flexural strength ranging from 120.38 (HC) to 186.02 MPa (GR), flexural modulus from 8.26 (HC) to 16.95 GPa (GR), and microhardness from 70.85 (AV) to 140.43 (GR). Weibull modulus and characteristic strength ranged from 16.35 (CS) to 34.98 (TE) and from 123.45 MPa (HC) to 190.3 MPa (GR), respectively. CONCLUSIONS: GR, TE, and CR presented significantly higher flexural strength, modulus, Weibull modulus, and characteristic strength than the others.

Ejemplares similares