Lithium di silicate ceramic surface treated with Er,Cr:YSGG and other conditioning regimes bonded to orthodontic bracket

AIM: To assess bond integrity and modes of failure of metallic brackets to lithium disilicate ceramics (LDC) conditioned with Er,Cr:YSGG laser (ECL). MATERIAL AND METHODS: Sixty LDC were arbitrarily allocated into six groups (n = 15) according to the type of ceramic surface conditioning treatment. Group 1 surface treated with silane (S) only, group 2 surface etched with hydrofluoric acid (HF)+ S, group 3 surface conditioned with HF+ ultrasonic bath (UB)+ S, group 4 sand blasting (SB) of glass ceramic surface with 50 µm Al(2)O(3), group 5 surface conditioned with self-etch ceramic primer (SECP) and in group 6 surface treated with ECL + S. After conditioning, the specimens were positioned in a universal testing device for shear bond strength (SBS) testing. Adhesive Remnant Index (ARI) was used to determine sites of bond failure. Among experimental groups analysis of variance (ANOVA) and Tukey multiple comparison test was used at a significance level of (p < 0.05). RESULTS: The highest SBS values were observed in group 3 HF+ UB + S (18.21 ± 1.241) and the lowest SBS values were displayed group 1 surface treated with S only (5.21 ± 0.23). Specimens surface conditioned in group 2 with HF+ S (17.85 ± 1.25), group 3 HF+ UB + S (18.21 ± 1.241) and group 6 ECL + S (17.09 ± 1.114) unveiled comparable SBS values (p > 0.05). CONCLUSION: LDC conditioned with ECL at (4.5 W and 30 Hz) has a potential to be used in clinical settings alternate to HF acid.