Effect of Acid Mixtures on Surface Properties and Biaxial Flexural Strength of As-Sintered and Air-Abraded Zirconia

The aim of this work was to evaluate the effects of application time of an acid mixture solution on the surface roughness, phase transformation, and biaxial flexural strength of 3Y-TZP after sintering or air abrasion. For the biaxial flexural strength measurement, 220 3Y-TZP disk-shaped specimens were prepared after as-sintering or air abrasion. The etching solution comprised a mixture of hydrofluoric acid, sulfuric acid, hydrogen peroxide, methyl alcohol, and purified water. The samples were divided into 11 subgroups according to the etching times (Control, 1, 2, 3, 5, 8, 10, 12, 15, 20, and 30 min). The results showed that acid treatment on both as-sintered and air-abraded 3Y-TZP surfaces increased the surface roughness. However, it had no significant effects on the monoclinic phase or flexural strength of as-sintered zirconia. The monoclinic phase and flexural strength of air-abraded zirconia increased sharply after air abrasion; however, they gradually decreased after acid treatment, to a similar level to the case of the untreated surface. Surface treatment with acid mixture increased the roughness, but the lack of increase of monoclinic phase is thought to be because the loose monoclinic particles remaining on the surface were removed through the etching process.