Correlation between Defects and Technical Wear of Materials Used in Traditional Construction

The degree of technical wear of old buildings, which are made of basic materials (cement, concrete, steel, timber, plaster, brick) using traditional technology, is expressed by the size and intensity of damage to their elements. The topic of the research concerns old residential buildings from the turn of the 19th and 20th centuries, which are located in the downtown district of Wroclaw, Poland. The descriptive analysis and the analysis of the definitions of defects that occur in the elements of residential buildings, which were performed as random analyzes, do not allow defects to be considered as measurable variables at a level of visual investigation. The major drawback of the method that is used by experts when assessing the technical condition of civil engineering buildings is that it does not numerically express the magnitude (strength) of the defects. Therefore, an attempt was made to numerically express the relationship (if such a relationship exists) between the occurred defects of buildings and the extent of their technical wear process. When calculating the strength of this relationship, the method of determining the point biserial correlation coefficient for the measurable property and the dichotomous property was used. It was found that the direction of the relation is right-hand for all the tested building elements, but the strength of the correlation between the detected defects and technical wear shows a considerable span and depends on the conditions of the apartment house’s maintenance. As a rule, damage caused by water penetration and moisture penetration always shows correlations of at least moderate strength.