Performance Improvement of PVDF–HFP-Based Gel Polymer Electrolyte with the Dopant of Octavinyl-Polyhedral Oligomeric Silsesquioxane

Gel polymer electrolytes have the advantages of both a solid electrolyte and a liquid electrolyte. As a transitional product before which a solid electrolyte can be comprehensively used, gel polymer electrolytes are of great research value. They can reduce the risk of spontaneous combustion and expl...

Descripción completa

Detalles Bibliográficos
Autores principales: Guo, Xin, Li, Shunchang, Chen, Fuhua, Chu, Ying, Wang, Xueying, Wan, Weihua, Zhao, Lili, Zhu, Yongping
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2021
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8196579/
https://www.ncbi.nlm.nih.gov/pubmed/34063801
http://dx.doi.org/10.3390/ma14112701
Descripción
Sumario:Gel polymer electrolytes have the advantages of both a solid electrolyte and a liquid electrolyte. As a transitional product before which a solid electrolyte can be comprehensively used, gel polymer electrolytes are of great research value. They can reduce the risk of spontaneous combustion and explosion caused by leakage during the use of conventional liquid electrolytes. Poly(vinylidene-fluoride-co-hexafluoropropylene) (PVDF–HFP), a material with excellent performance, has been widely utilized in the preparation of gel polymer electrolytes. Here, PVDF–HFP-based gel polymer membranes with polyvinyl pyrrolidone (PVP) pores were prepared using a phase inversion method, and Octavinyl-polyhedral oligomeric silsesquioxane (OVAPOSS) was doped to improve its temperature resistance as well as its ionic conductivity, to enhance its safety and electrochemical performance. The final prepared polymer membrane had a porosity of 85.06% and still had a certain mechanical strength at 160 °C without any shrinkage. The gel polymer electrolyte prepared with this polymer membrane had an ionic conductivity of 1.62 × 10(−3) S·cm(−1) at 30 °C, as well as an electrochemical window of about 5.5 V. The LiCoO(2)-Li button half-cell prepared therefrom had a specific capacity of 141 mAh·g(−1) at a rate of 1C. The coulombic efficiency remained above 99% within 100 cycles and the capacity retention rate reached 99.5%, which reveals an excellent cycling stability.