Stress Corrosion Cracking Behavior of TP 439 and 690 TT under Film-Forming Amine Environment

Film-forming amines have been widely used in thermal power plants for maintenance after shutdown, and there are more and more applications and researches in nuclear power secondary circuits for this purpose. However, in the direction of stress corrosion cracking, there is not much research on the in...

Descripción completa

Detalles Bibliográficos
Autores principales:	Jundong, Lu, Xiaobin, Jiang, Ke, Sun, Bin, Liu, Xinmin, Li, Qinwen, Ni
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Hindawi 2021
Materias:	Research Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8208861/ https://www.ncbi.nlm.nih.gov/pubmed/34211621 http://dx.doi.org/10.1155/2021/6668537

Ejemplares similares

Simulating Porous Magnetite Layer Deposited on Alloy 690TT Steam Generator Tubes
por: Jeon, Soon-Hyeok, et al.
Publicado: (2018)

The Evolution of Fretting Wear Behavior and Damage Mechanism in Alloy 690TT with Cycle Number
por: Xin, Long, et al.
Publicado: (2020)

Effects of Zinc Addition on the Corrosion Behavior of Pre-Filmed Alloy 690 in Borated and Lithiated Water at 330 °C
por: Jeon, Soon-Hyeok, et al.
Publicado: (2021)

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking
por: Wang, Wenwen, et al.
Publicado: (2015)

Crevice Corrosion Behavior of Alloy 690 in High-Temperature Aerated Chloride Solution
por: Ning, Fangqiang, et al.
Publicado: (2022)

Effects of Hydrogen Contents on Oxidation Behavior of Alloy 690TT and Associated Boron Accumulation within Oxides in High-Temperature Water
por: Jeon, Soon-Hyeok, et al.
Publicado: (2018)

Laser Shock Peening Improves the Corrosion Resistance of an E690 High-Strength Steel Cladding Layer
por: Qin, Jiaxin, et al.
Publicado: (2023)

Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments
por: Yeh, Chun-Ping, et al.
Publicado: (2020)

Prediction of Crack Width in RC Piles Exposed to Local Corrosion in Chloride Environment
por: Shao, Wei, et al.
Publicado: (2023)

Divertimento k. 439b, No. 2
por: Mozart, Wolfgang Amadeus, 1756-1791
Publicado: (1986)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

Modeling Corrosion Product Film Formation and Hydrogen Diffusion at the Crack Tip of Austenitic Stainless Steel
por: Yang, Fuqiang, et al.
Publicado: (2023)

Hydrogen-Induced Cracking Caused by Galvanic Corrosion of Steel Weld in a Sour Environment
por: Park, Jin Sung, et al.
Publicado: (2021)

Regulation of behavioral response to stress by microRNA-690
por: Park, Jungyoung, et al.
Publicado: (2021)

Spray drying OZ439 nanoparticles to form stable, water-dispersible powders for oral malaria therapy
por: Ristroph, Kurt D., et al.
Publicado: (2019)

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile
por: Ma, Jijun, et al.
Publicado: (2021)

Corrosion Crack Morphology and Creep Analysis of Members Based on Meso-Scale Corrosion Penetration
por: Zeng, Bin, et al.
Publicado: (2022)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

Acero de refuerzo de alta resistencia (ACI-439)
Publicado: (1986)

Acero de refuerzo de alta resistencia (ACI-439)
Publicado: (1975)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Laboratory-Based Investigation into Stress Corrosion Cracking of Cable Bolts
por: Wu, Saisai, et al.
Publicado: (2019)

Self Assembled Films of Porphyrins with Amine Groups at Different Positions: Influence of Their Orientation on the Corrosion Inhibition and the Electrocatalytic Activity
por: Lokesh, Koodlur Sannegowda, et al.
Publicado: (2012)

Zeta Potentials of Magnetite Particles and Alloy 690 Surfaces in Alkaline Solutions
por: Lee, Ji-Min, et al.
Publicado: (2020)

Corrosion Behavior and Susceptibility to Stress Corrosion Cracking of Leaded and Lead-Free Brasses in Simulated Drinking Water
por: Choucri, Jamal, et al.
Publicado: (2021)

The tunnel TT6 and TT70 towards TT60
por: CERN PhotoLab
Publicado: (1979)

Correction: Meulenberg, E. P. Phenolics: Occurrence and Immunochemical Detection in Environment and Food. Molecules 2009, 14, 439-473
por: Meulenberg, Eline P.
Publicado: (2009)

Methodology to evaluate stress corrosion cracking in ethanol environments, applied to circumferential welds on API 5 L steel pipelines
por: Santos, Elielson A., et al.
Publicado: (2022)

Correlation between electrochemical properties and stress corrosion cracking of super 13Cr under an HTHP CO(2) environment
por: Yue, Xiaoqi, et al.
Publicado: (2018)

Investigation of Stress Corrosion Cracking Resistance of Irradiated 12Cr Ferritic-Martensitic Stainless Steel in Supercritical Water Environment
por: Margolin, Boris, et al.
Publicado: (2023)

Zigzag Hollow Cracks of Silver Nanoparticle Film Regulated by Its Drying Micro-environment
por: Tao, Ruiqiang, et al.
Publicado: (2018)

Forms of corrosion : recognition and prevention
Publicado: (1982)

SAT439 Euglycemic Diabetic Ketoacidosis When Combining Empagliflozin With Cocaine
por: Squicimari-de Cardenas, Fabio Alejandro, et al.
Publicado: (2023)

Concrete Cracking Prediction Including the Filling Proportion of Strand Corrosion Products
por: Wang, Lei, et al.
Publicado: (2016)

Concrete Protective Layer Cracking Caused by Non-Uniform Corrosion of Reinforcements
por: Zhang, Lu, et al.
Publicado: (2019)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Modelling of Corrosion-Induced Concrete Cover Cracking Due to Chloride Attacking
por: Lun, Pei-Yuan, et al.
Publicado: (2021)

Letter to the Editor Re: Billeaud et al. Nutrients 2018, 10, 690
por: Bernhard, Wolfgang, et al.
Publicado: (2019)

690. Oka-Strain Varicella-Zoster Virus Meningitis in a Healthy Adolescent
por: Nadimpalli, Sruti S, et al.
Publicado: (2020)

Cannot write session to /tmp/vufind_sessions/sess_lvtg6m0dd3dro2i678jt57l8ub