Bond strength between titanium and polymer-based materials adhesively cemented

The aim was to evaluate the bond strength between titanium and polymer-based materials for prosthetic restorations, cemented with different adhesive cement systems. Eight groups with 13 specimens in each group were included. Each specimen consisted of two parts: a cylinder of titanium resembling a titanium base, and a cylinder of one of two polymer-based materials Micro Filled Hybrid (MFH) or Telio CAD and cemented with one of four adhesive cement systems, namely Multilink Hybrid Abutment, Panavia V5, RelyX Ultimate and G-Cem LinkAce. The titanium was sandblasted with 50 µm Al(2)O(3) and treated according to each cement manufacturer's recommendations. The polymer-based materials were pre-treated according to the manufacturer's instructions including sandblasting for MFH. After cementation, the groups were water stored for one day before thermocycling: 5000 cycles in 5–55 °C. A shear bond strength test was performed (crosshead speed 0.5 mm/min) and data was analysed with one-way ANOVA, Tukey's test. Telio CAD cemented with Panavia V5 and G-Cem LinkAce showed significantly lower bond strength compared to all other groups, due to spontaneous debonding. The highest numerical bond strength was found in the group of MFH cemented with RelyX Ultimate or with G-Cem LinkAce. Generally, the Telio CAD groups showed lower bond strength values than the MFH groups. The conclusions are that pre-treatment methods and choice of cement system are of importance for polymer-based materials for prosthetic restorations. The bond strength is adequate for provisional cementation irrespective of cement system when pre-treating by sandblasting, but cement dependent without sandblasting.