Electrochemical Deposition Treatment (EDT) as a Comprehensive Rehabilitation Method for Corrosion-Induced Deterioration in Concrete with Various Severity Levels

The primary purposes of this study are to investigate the feasibility of electrochemical deposition treatment (EDT) as a comprehensive rehabilitation method for corrosion-induced deterioration in reinforced concrete with various severity levels, and to propose a guideline for the determination of cr...

Descripción completa

Detalles Bibliográficos
Autores principales:	Kim, Je-Kyoung, Yee, Jurng-Jae, Kee, Seong-Hoon
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2021
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8473423/ https://www.ncbi.nlm.nih.gov/pubmed/34577494 http://dx.doi.org/10.3390/s21186287

Ejemplares similares

Corrosion Monitoring of Reinforced Steel Embedded in Cement Mortar under Wet-And-Dry Cycles by Electrochemical Impedance Spectroscopy
por: Kim, Je-Kyoung, et al.
Publicado: (2019)

Electrical Resistivity Measurements for Nondestructive Evaluation of Chloride-Induced Deterioration of Reinforced Concrete—A Review
por: Robles, Kevin Paolo V., et al.
Publicado: (2022)

Effect of the Geometrical Constraints to the Wenner Four-Point Electrical Resistivity Test of Reinforced Concrete Slabs
por: Robles, Kevin Paolo V., et al.
Publicado: (2021)

Effects of Saturation Levels on the Ultrasonic Pulse Velocities and Mechanical Properties of Concrete
por: Candelaria, Ma. Doreen Esplana, et al.
Publicado: (2020)

Electrical Resistivity Measurements of Reinforced Concrete Slabs with Delamination Defects
por: Robles, Kevin Paolo V., et al.
Publicado: (2020)

Electrochemical Noise Measurement to Assess Corrosion of Steel Reinforcement in Concrete
por: Mills, Douglas, et al.
Publicado: (2021)

Synthesis of Arylazide‐ and Diazirine‐Containing CrAsH‐EDT(2) Photoaffinity Probes
por: Syeda, Shameem S., et al.
Publicado: (2016)

Evaluation of the Corrosion Behavior of Reinforced Concrete with an Inhibitor by Electrochemical Impedance Spectroscopy
por: Park, JangHyun, et al.
Publicado: (2021)

Monitoring Concrete Deterioration Due to Reinforcement Corrosion by Integrating Acoustic Emission and FBG Strain Measurements
por: Li, Weijie, et al.
Publicado: (2017)

Bioinspired Hydrogenase Models: The Mixed-Valence Triiron Complex [Fe(3)(CO)(7)(μ-edt)(2)] and Phosphine Derivatives [Fe(3)(CO)(7–x)(PPh(3))(x)(μ-edt)(2)] (x = 1, 2) and [Fe(3)(CO)(5)(κ(2)-diphosphine)(μ-edt)(2)] as Proton Reduction Catalysts
por: Rahaman, Ahibur, et al.
Publicado: (2014)

Over-Expression of Arabidopsis EDT1 Gene Confers Drought Tolerance in Alfalfa (Medicago sativa L.)
por: Zheng, Guangshun, et al.
Publicado: (2017)

Evaluation of the Size of a Defect in Reinforcing Steel Using Magnetic Flux Leakage (MFL) Measurements
por: Yousaf, Jamal, et al.
Publicado: (2023)

The Cover Depth Effect on Corrosion-Induced Deterioration of Reinforced Concrete Focusing on Water Penetration: Field Survey and Laboratory Study
por: Asamoto, Shingo, et al.
Publicado: (2021)

Life-cycle cost analysis for protection and rehabilitation of concrete bridges relative to reinforcement corrosion /
por: Purvis, Ronald L.
Publicado: (1994)

The Effect of a Corrosion Inhibitor on the Rehabilitation of Reinforced Concrete Containing Sea Sand and Seawater
por: Pan, Chonggen, et al.
Publicado: (2020)

Electromagnetic Metrology on Concrete and Corrosion
por: Kim, Sung, et al.
Publicado: (2011)

Corrosion of steel in concrete : prevention, diagnosis, repair /
Publicado: (2004)

Fuzzy Optimization for the Remediation of Ammonia: A Case Study Based on Electrochemical Oxidation
por: Choi, Angelo Earvin Sy, et al.
Publicado: (2021)

Microbiologically induced deterioration of concrete - A Review
por: Wei, Shiping, et al.
Publicado: (2014)

Review on Microbially Influenced Concrete Corrosion
por: Wang, Dongsheng, et al.
Publicado: (2023)

Azadirachta indica Leaf Extract as Green Corrosion Inhibitor for Reinforced Concrete Structures: Corrosion Effectiveness against Commercial Corrosion Inhibitors and Concrete Integrity
por: Valdez-Salas, Benjamin, et al.
Publicado: (2021)

Concrete Cover Cracking and Reinforcement Corrosion Behavior in Concrete with New-to-Old Concrete Interfaces
por: Zhang, Juhui, et al.
Publicado: (2023)

Effect of Stray Current on Corrosion and Calcium Ion Corrosion of Concrete Reinforcement
por: Yang, Weijun, et al.
Publicado: (2022)

Evaluation of Early Concrete Damage Caused by Chloride-Induced Steel Corrosion Using a Deep Learning Approach Based on RNN for Ultrasonic Pulse Waves
por: Mukhti, Julfikhsan Ahmad, et al.
Publicado: (2023)

Overexpression of AtEDT1/HDG11 in Chinese Kale (Brassica oleracea var. alboglabra) Enhances Drought and Osmotic Stress Tolerance
por: Zhu, Zhangsheng, et al.
Publicado: (2016)

LPI-EnEDT: an ensemble framework with extra tree and decision tree classifiers for imbalanced lncRNA-protein interaction data classification
por: Peng, Lihong, et al.
Publicado: (2021)

Electrochemical Study on the Macro-Cell Corrosion of Pipeline Steel Partially Covered by Different Kinds of Mineral Deposits
por: He, Limin, et al.
Publicado: (2023)

Polarization Induced Deterioration of Reinforced Concrete with CFRP Anode
por: Zhu, Ji-Hua, et al.
Publicado: (2015)

Deterioration Process of Concrete Exposed to Internal Sulfate Attack
por: Chen, Weifeng, et al.
Publicado: (2020)

Steel Corrosion Evaluation of Basalt Fiber RPC Affected by Crack and Steel-Concrete Interface Damage Using Electrochemical Methods
por: Liu, Hanbing, et al.
Publicado: (2020)

Special Issue “Corrosion in Concrete: Inhibitors and Coatings”
por: Coppola, Luigi
Publicado: (2021)

Improving Corrosion Resistance of Magnesium Alloy in Cl(−) Containing Simulated Concrete Pore Solution by Ultrasound-Assisted Chemical Deposition
por: Wang, Ye, et al.
Publicado: (2021)

Electrochemical and quantum mechanical investigation of various small molecule organic compounds as corrosion inhibitors in mild steel
por: Carranza, Mary Stephanie S., et al.
Publicado: (2021)

Electrochemical behaviour and analysis of Zn and Zn–Ni alloy anti-corrosive coatings deposited from citrate baths
por: Anwar, Shams, et al.
Publicado: (2018)

Galvanic corrosion of duplex corrosion-resistant steel rebars under carbonated concrete conditions
por: Jiang, Jinyang, et al.
Publicado: (2018)

Electrochemical techniques in corrosion science and engineering /
Publicado: (2003)

Electrochemical metrics for corrosion resistant alloys
por: Nyby, Clara, et al.
Publicado: (2021)

Monitoring Corrosion of Steel Bars in Reinforced Concrete Structures
por: Verma, Sanjeev Kumar, et al.
Publicado: (2014)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Electrochemical Deposition of Nanomaterials for Electrochemical Sensing
por: Tonelli, Domenica, et al.
Publicado: (2019)

Cannot write session to /tmp/vufind_sessions/sess_ua4gptmpog3i9oo5qgadj8479r