Distinct Advantages of Circumferential Notch Tensile (CNT) Testing in the Determination of a Threshold for Stress Corrosion Cracking (K(ISCC))

Stress corrosion cracking (SCC) is a vexing problem for load-bearing equipment operating in a corrosive environment in various industries, such as aerospace, chemical and mineral processing, civil structures, bioimplants, energy generation etc. For safe operation, effective maintenance and life pred...

Descripción completa

Detalles Bibliográficos
Autores principales:	Singh Raman, R. K., Jones, Rhys
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	MDPI 2021
Materias:	Review
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8509828/ https://www.ncbi.nlm.nih.gov/pubmed/34640017 http://dx.doi.org/10.3390/ma14195620

Ejemplares similares

ISOLDE LSF and ISCC matters
por: Huber, G
Publicado: (1999)

Notch Effects on the Stress Intensity Factor and on the Fatigue Crack Path for Eccentric Circular Internal Cracks in Elliptically Notched Round Bars under Tensile Loading
por: Toribio, Jesús, et al.
Publicado: (2022)

Methodology to evaluate stress corrosion cracking in ethanol environments, applied to circumferential welds on API 5 L steel pipelines
por: Santos, Elielson A., et al.
Publicado: (2022)

Corrosion Resistance of Al–CNT Metal Matrix Composites
por: Popov, Vladimir V., et al.
Publicado: (2021)

Atomistic Investigation on the Blocking Phenomenon of Crack Propagation in Cu Substrate Reinforced by CNT
por: Shim, Jee Soo, et al.
Publicado: (2023)

Stress Intensity Factor (SIF) Solutions and Fatigue Crack Paths in Eccentric Circumferentially Cracked Round Bar (CCRB) in Tension
por: Toribio, Jesús, et al.
Publicado: (2023)

Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
por: Singh Raman, R. K., et al.
Publicado: (2014)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

Simulation of Percolation Threshold, Tunneling Distance, and Conductivity for Carbon Nanotube (CNT)-Reinforced Nanocomposites Assuming Effective CNT Concentration
por: Zare, Yasser, et al.
Publicado: (2020)

Analysis of the Connecting Effectiveness of the Interphase Zone on the Tensile Properties of Carbon Nanotubes (CNT) Reinforced Nanocomposite
por: Zare, Yasser, et al.
Publicado: (2020)

Effects of Nitrogen and Tensile Direction on Stress Corrosion Cracking Susceptibility of Ni-Free FeCrMnC-Based Duplex Stainless Steels
por: Ha, Heon-Young, et al.
Publicado: (2017)

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking
por: Wang, Wenwen, et al.
Publicado: (2015)

Prediction Model of Stress Intensity Factor of Circumferential Through Crack in Elbow Based on Neural Network
por: Li, Xiaohong, et al.
Publicado: (2022)

Tensile fracture of a single crack in first-year sea ice
por: Dempsey, J. P., et al.
Publicado: (2018)

Tensile Notch Sensitivity of Additively Manufactured IN 625 Superalloy
por: Matache, Gheorghe, et al.
Publicado: (2020)

Corrosion of High-Strength Steel Wires under Tensile Stress
por: Lv, Shanglin, et al.
Publicado: (2020)

Optimization of Tensile Strength and Young’s Modulus of CNT–CF/Epoxy Composites Using Response Surface Methodology (RSM)
por: Rahman, Md. Rezaur, et al.
Publicado: (2022)

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile
por: Ma, Jijun, et al.
Publicado: (2021)

Corrosion Crack Morphology and Creep Analysis of Members Based on Meso-Scale Corrosion Penetration
por: Zeng, Bin, et al.
Publicado: (2022)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

Lulu2 regulates the circumferential actomyosin tensile system in epithelial cells through p114RhoGEF
por: Nakajima, Hiroyuki, et al.
Publicado: (2011)

Near-threshold fatigue crack propagation without oxide-induced crack closure
por: Tazoe, Koki, et al.
Publicado: (2020)

Robust Determination of Fatigue Crack Propagation Thresholds from Crack Growth Data
por: Schönherr, Josef Arthur, et al.
Publicado: (2022)

Corrosion Evaluation of 316L Stainless Steel in CNT-Water Nanofluid: Effect of CNTs Loading
por: Abdeen, Dana H., et al.
Publicado: (2019)

Influence of Defect Number, Distribution Continuity and Orientation on Tensile Strengths of the CNT-Based Networks: A Molecular Dynamics Study
por: Shi, Xian, et al.
Publicado: (2022)

Tensile-Tearing Fracture Analysis of U-Notched Spruce Samples
por: Torabi, Ali Reza, et al.
Publicado: (2022)

Impact of Notches on Additively Manufactured Inconel 718 Tensile Performance
por: Johnson, Joseph, et al.
Publicado: (2023)

Routine use of Circumferential ‘Doughnut’ Biopsy in Pull through Surgery for Hirschsprung's Disease: Advantages and Limitations
por: Murthi, Govind V. S., et al.
Publicado: (2021)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Laboratory-Based Investigation into Stress Corrosion Cracking of Cable Bolts
por: Wu, Saisai, et al.
Publicado: (2019)

Localized fluid discharge by tensile cracking during the post-seismic period in subduction zones
por: Otsubo, Makoto, et al.
Publicado: (2020)

Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments
por: Yeh, Chun-Ping, et al.
Publicado: (2020)

Corrosion Behavior and Susceptibility to Stress Corrosion Cracking of Leaded and Lead-Free Brasses in Simulated Drinking Water
por: Choucri, Jamal, et al.
Publicado: (2021)

Enhancing Interfacial Bonding and Tensile Strength in CNT-Cu Composites by a Synergetic Method of Spraying Pyrolysis and Flake Powder Metallurgy
por: Chen, Xiangyang, et al.
Publicado: (2019)

Circumferential SH Wave Piezoelectric Transducer System for Monitoring Corrosion-Like Defect in Large-Diameter Pipes
por: Zhang, Hao, et al.
Publicado: (2020)

Does it matter?: information technology and the corrosion of competitive advantage
por: Carr, Nicholas G
Publicado: (2004)

Hot tensile properties and constant load stress corrosion cracking test data of autogenous weld joints of super 304HCu stainless steel in boiling MgCl(2) solution
por: Kumar, M. Vinoth, et al.
Publicado: (2018)

Notch sensitivity of orthotropic solids: interaction of tensile and shear damage zones
por: Tankasala, Harika C., et al.
Publicado: (2018)

Progressive Failure Simulation of Notched Tensile Specimen for Triaxially-Braided Composites
por: Zhao, Zhenqiang, et al.
Publicado: (2019)

Cannot write session to /tmp/vufind_sessions/sess_pqpb6ruj04063jk689cpckge34