Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling
Aiming at the problem of the poor plasticity of magnesium alloy leading to serious edge cracks in the rolling process, this paper conducts a systematic study on the crack suppression mechanism of rolling under different thickness reductions. Using restricted rolling and conventional rolling, compari...
Autores principales: | , , , , , |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2021
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8510477/ https://www.ncbi.nlm.nih.gov/pubmed/34640070 http://dx.doi.org/10.3390/ma14195668 |
_version_ | 1784582582073032704 |
---|---|
author | Tian, Jing Deng, Jiafei Shi, Quanxin Chang, Yuanying Liang, Wei Zhang, Wanggang |
author_facet | Tian, Jing Deng, Jiafei Shi, Quanxin Chang, Yuanying Liang, Wei Zhang, Wanggang |
author_sort | Tian, Jing |
collection | PubMed |
description | Aiming at the problem of the poor plasticity of magnesium alloy leading to serious edge cracks in the rolling process, this paper conducts a systematic study on the crack suppression mechanism of rolling under different thickness reductions. Using restricted rolling and conventional rolling, comparing the microstructure evolution of the plate after rolling, and combining the information of the simulated temperature field and stress field of the plates, the behavior of twins and dislocations under different thickness reductions is explained, and the influence of serious damage caused by single-pass hot rolling of magnesium alloy is explored. The compressive stress fields along with the transverse and normal directions under restricted rolling cause the compression twins to mature into secondary twins under rolling with small thickness reduction and induce a large number of tensile twins when the thickness reduction amount is increased. The multiple slips activated by the higher temperature field at the edge of the small thickness reduction amount cause dislocations to be distributed inside and outside the twins, while the edge with large thickness reduction can activate more slip due to the high-temperature field resulting from friction, resulting in the twin be destroyed. |
format | Online Article Text |
id | pubmed-8510477 |
institution | National Center for Biotechnology Information |
language | English |
publishDate | 2021 |
publisher | MDPI |
record_format | MEDLINE/PubMed |
spelling | pubmed-85104772021-10-13 Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling Tian, Jing Deng, Jiafei Shi, Quanxin Chang, Yuanying Liang, Wei Zhang, Wanggang Materials (Basel) Article Aiming at the problem of the poor plasticity of magnesium alloy leading to serious edge cracks in the rolling process, this paper conducts a systematic study on the crack suppression mechanism of rolling under different thickness reductions. Using restricted rolling and conventional rolling, comparing the microstructure evolution of the plate after rolling, and combining the information of the simulated temperature field and stress field of the plates, the behavior of twins and dislocations under different thickness reductions is explained, and the influence of serious damage caused by single-pass hot rolling of magnesium alloy is explored. The compressive stress fields along with the transverse and normal directions under restricted rolling cause the compression twins to mature into secondary twins under rolling with small thickness reduction and induce a large number of tensile twins when the thickness reduction amount is increased. The multiple slips activated by the higher temperature field at the edge of the small thickness reduction amount cause dislocations to be distributed inside and outside the twins, while the edge with large thickness reduction can activate more slip due to the high-temperature field resulting from friction, resulting in the twin be destroyed. MDPI 2021-09-29 /pmc/articles/PMC8510477/ /pubmed/34640070 http://dx.doi.org/10.3390/ma14195668 Text en © 2021 by the authors. https://creativecommons.org/licenses/by/4.0/Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/). |
spellingShingle | Article Tian, Jing Deng, Jiafei Shi, Quanxin Chang, Yuanying Liang, Wei Zhang, Wanggang Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title | Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title_full | Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title_fullStr | Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title_full_unstemmed | Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title_short | Effect of Temperature Field and Stress Field of Different Crack Behavior on Twins and Dislocations under Mg Alloy Rolling |
title_sort | effect of temperature field and stress field of different crack behavior on twins and dislocations under mg alloy rolling |
topic | Article |
url | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8510477/ https://www.ncbi.nlm.nih.gov/pubmed/34640070 http://dx.doi.org/10.3390/ma14195668 |
work_keys_str_mv | AT tianjing effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling AT dengjiafei effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling AT shiquanxin effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling AT changyuanying effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling AT liangwei effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling AT zhangwanggang effectoftemperaturefieldandstressfieldofdifferentcrackbehaviorontwinsanddislocationsundermgalloyrolling |