Corrosion behavior of X80 pipeline steel local defect pits under static liquid film

In this work, the corrosion electrochemical information under different thicknesses of liquid film was tested. The local corrosion development process of X80 steel under different thicknesses of liquid film was studied by combining the detection and analysis of scale and the matrix corrosion morphol...

Descripción completa

Detalles Bibliográficos
Autores principales:	Tan, Zhuowei, Wang, Zhenbo, Zhang, Shengzhu, Bai, Shuyu, Zhang, Dalei, Jin, Youhai, Xing, Shaohua
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Nature Publishing Group UK 2021
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8531304/ https://www.ncbi.nlm.nih.gov/pubmed/34675346 http://dx.doi.org/10.1038/s41598-021-99973-8

Ejemplares similares

A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel
por: Yang, Zixuan, et al.
Publicado: (2017)

Structural Integrity of Steel Pipeline with Clusters of Corrosion Defects
por: Witek, Maciej
Publicado: (2021)

Effect of H(2)S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint
por: Wang, Xueli, et al.
Publicado: (2022)

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions
por: Chen, Jukai, et al.
Publicado: (2022)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Effect of Alternating Current and Sulfate-Reducing Bacteria on Corrosion of X80 Pipeline Steel in Soil-Extract Solution
por: Qing, Yongchang, et al.
Publicado: (2019)

Mechanical property degradation of X80 pipeline steel due to microbiologically influenced corrosion caused by Desulfovibrio vulgaris
por: Li, Zhong, et al.
Publicado: (2022)

Determination of Iron Valence States Around Pits and the Influence of Fe(3+) on the Pitting Corrosion of 304 Stainless Steel
por: Zhang, Hao, et al.
Publicado: (2020)

Effect of Pseudomonas aeruginosa on corrosion of X65 pipeline steel
por: Tang, Jianhua, et al.
Publicado: (2022)

Atomic-scale decoration for improving the pitting corrosion resistance of austenitic stainless steels
por: Zhou, Y. T., et al.
Publicado: (2014)

Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment
por: Wang, Liwei, et al.
Publicado: (2018)

Utilizing birch leaf extract in pickling liquid as a sustainable source of corrosion inhibitor for pipeline steel
por: Mohsen, Q., et al.
Publicado: (2022)

Influence of Ethanol on Pitting Corrosion Behavior of Stainless Steel for Bioethanol Fermentation Tanks
por: Wan, Yiting, et al.
Publicado: (2020)

Hydrogen Accumulation and Distribution in Pipeline Steel in Intensified Corrosion Conditions
por: Titov, Anatolii I., et al.
Publicado: (2019)

Pitting Corrosion and Microstructure of J55 Carbon Steel Exposed to CO(2)/Crude Oil/Brine Solution under 2–15 MPa at 30–80 °C
por: Bai, Haitao, et al.
Publicado: (2018)

The effect of magnetic field pretreatment on the corrosion behavior of carbon steel in static seawater
por: Zhao, Shuanzhu, et al.
Publicado: (2020)

pH Effect of Natural Gas Hydrate on X80 Steel Solid—Liquid Phase Scouring Corrosion
por: Deng, Song, et al.
Publicado: (2021)

Correlation between evolution of inclusions and pitting corrosion in 304 stainless steel with yttrium addition
por: Shi, Weining, et al.
Publicado: (2018)

Direct observation of pitting corrosion evolutions on carbon steel surfaces at the nano-to-micro- scales
por: Guo, Peng, et al.
Publicado: (2018)

Effect of Pre-Corrosion Pits on Residual Fatigue Life for 42CrMo Steel
por: Liu, Dezheng, et al.
Publicado: (2019)

Pitting Initiation and Propagation of X70 Pipeline Steel Exposed to Chloride-Containing Environments
por: Yang, Zixuan, et al.
Publicado: (2017)

Author Correction: Utilizing birch leaf extract in pickling liquid as a sustainable source of corrosion inhibitor for pipeline steel
por: Mohsen, Q., et al.
Publicado: (2023)

Effect of Nitrided and Nitrocarburised Austenite on Pitting and Crevice Corrosion Resistance of 316 LVM Steel Implants
por: Kajzer, Anita, et al.
Publicado: (2020)

Corrosion of Steel Rebars in Anoxic Environments. Part II: Pit Growth Rate and Mechanical Strength
por: Garcia, Elena, et al.
Publicado: (2021)

Semiconducting Behaviour and Corrosion Resistance of Passive Film on Corrosion-Resistant Steel Rebars
por: Lv, Shanglin, et al.
Publicado: (2022)

Recent Advances in Nondestructive Method and Assessment of Corrosion Undercoating in Carbon–Steel Pipelines
por: May, Zazilah, et al.
Publicado: (2022)

Investigation of erosion-corrosion failure of API X52 carbon steel pipeline
por: Abdu, Mahmoud T., et al.
Publicado: (2023)

The Synergistic Inhibitions of Tungstate and Molybdate Anions on Pitting Corrosion Initiation for Q235 Carbon Steel in Chloride Solution
por: Yang, Huanggen, et al.
Publicado: (2022)

Pits in Metals Caused by Collision With Liquid Drops and Rigid Steel Spheres
por: Engel, Olive G.
Publicado: (1960)

Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
por: Li, Zhong, et al.
Publicado: (2017)

Effect of Service Environmental Parameters on Electrochemical Corrosion Behavior of L80 Casing Steel
por: Sun, Xiaoguang, et al.
Publicado: (2021)

Effect of Nanosized NbC Precipitates on Hydrogen Diffusion in X80 Pipeline Steel
por: Cui, Qiaoqi, et al.
Publicado: (2017)

Effect of Surface Roughness on Pitting Corrosion of 2205 Duplex Stainless Steel Investigated by Electrochemical Noise Measurements
por: Tang, Yiwei, et al.
Publicado: (2019)

The Microstructure and Pitting Corrosion Behavior of K-TIG Welded Joints of the UNS S32101 Duplex Stainless Steel
por: Cui, Shuwan, et al.
Publicado: (2022)

Effects of Sodium Phosphate and Sodium Nitrite on the Pitting Corrosion Process of X70 Carbon Steel in Sodium Chloride Solution
por: Zhu, Yongyan, et al.
Publicado: (2020)

Research on the Corrosion Behavior of Q235 Pipeline Steel in an Atmospheric Environment through Experiment
por: Cai, Shuo, et al.
Publicado: (2022)

Enhanced Pitting Corrosion Resistance of Nanostructured AISI 304 Stainless Steel via Pipe Inner Surface Grinding Treatment
por: Han, Xiaolei, et al.
Publicado: (2023)

Study on the Corrosion Mechanism of N80 Steel in Simulated Oxygen-Reduced Air Drive Production Wellbores
por: Shi, Baocheng, et al.
Publicado: (2023)

The Corrosion Behavior of X100 Pipeline Steel in a Sodium Chloride Solution Containing Magnesium and Calcium
por: Yang, Xiaoning, et al.
Publicado: (2023)

Underground pipeline corrosion
por: Orazem, Mark
Publicado: (2014)

Cannot write session to /tmp/vufind_sessions/sess_0usfjbep3d6f97ulo1ia9u8u3o