Improved Thermoelectric Performance of Monolayer HfS(2) by Strain Engineering

[Image: see text] Strain engineering can effectively improve the energy band degeneracy of two-dimensional transition metal dichalcogenides so that they exhibit good thermoelectric properties under strain. In this work, we have studied the phonon, electronic, thermal, and thermoelectric properties o...

Descripción completa

Detalles Bibliográficos
Autores principales: Wang, Hao, Lan, Yang-Shun, Dai, Bo, Zhang, Xiao-Wei, Wang, Zhi-Guo, Ge, Ni-Na
Formato: Online Artículo Texto
Lenguaje:English
Publicado: American Chemical Society 2021
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8582045/
https://www.ncbi.nlm.nih.gov/pubmed/34778655
http://dx.doi.org/10.1021/acsomega.1c04286
Descripción
Sumario:[Image: see text] Strain engineering can effectively improve the energy band degeneracy of two-dimensional transition metal dichalcogenides so that they exhibit good thermoelectric properties under strain. In this work, we have studied the phonon, electronic, thermal, and thermoelectric properties of 1T-phase monolayer HfS(2) with biaxial strain based on first-principles calculations combined with Boltzmann equations. At 0% strain, the results show that the lattice thermal conductivity of monolayer HfS(2) is 5.01 W m(–1) K(–1) and the electronic thermal conductivities of n-type and p-type doped monolayer HfS(2) are 2.94 and 0.39 W m(–1) K(–1), respectively, when the doping concentration is around 5 × 10(12) cm(–2). The power factors of the n-type and p-type doped monolayer HfS(2) are different, 29.4 and 1.6 mW mK(–2), respectively. Finally, the maximum ZT value of the n-type monolayer HfS(2) is 1.09, which is higher than 0.09 of the p-type monolayer HfS(2). Under biaxial strain, for n-type HfS(2), the lattice thermal conductivity, the electronic thermal conductivity, and the power factor are 1.55 W m(–1) K(–1), 1.44 W m(–1) K(–1), and 22.9 mW mK(–2) at 6% strain, respectively. Based on the above factor, the ZT value reaches its maximum of 2.29 at 6% strain. For p-type HfS(2), the lattice thermal conductivity and the electronic thermal conductivity are 1.12 and 1.53 W m(–1) K(–1) at 7% strain, respectively. Moreover, the power factor is greatly improved to 29.5 mW mK(–2). Finally, the maximum ZT value of the p-type monolayer HfS(2) is 3.35 at 7% strain. It is obvious that strain can greatly improve the thermoelectric performance of monolayer HfS(2), especially for p-type HfS(2). We hope that the research results can provide data references for future experimental exploration.