Fatigue Crack Initiation Change of Cast AZ91 Magnesium Alloy from Low to Very High Cycle Fatigue Region
Fatigue tests were performed on the AZ91 cast alloy to identify the mechanisms of the fatigue crack initiation. In different fatigue regions, different mechanisms were observed. In the low and high cycle fatigue regions, slip markings formation accompanied with Mg(17)Al(12) particles cracking were o...
Autores principales: | Fintová, Stanislava, Trško, Libor, Chlup, Zdeněk, Pastorek, Filip, Kajánek, Daniel, Kunz, Ludvík |
---|---|
Formato: | Online Artículo Texto |
Lenguaje: | English |
Publicado: |
MDPI
2021
|
Materias: | |
Acceso en línea: | https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8585000/ https://www.ncbi.nlm.nih.gov/pubmed/34771771 http://dx.doi.org/10.3390/ma14216245 |
Ejemplares similares
-
Comparison of Electrochemical Methods for the Evaluation of Cast AZ91 Magnesium Alloy
por: Tkacz, Jakub, et al.
Publicado: (2016) -
The Effect of Mechanical Pretreatment on the Electrochemical Characteristics of PEO Coatings Prepared on Magnesium Alloy AZ80
por: Sovík, Ján, et al.
Publicado: (2023) -
Improvement of AZ91 Alloy Corrosion Properties by Duplex NI-P Coating Deposition
por: Wasserbauer, Jaromír, et al.
Publicado: (2020) -
The Effect of Solidification Rate on the Corrosion Resistance of Die-Cast AZ91 Magnesium Alloy
por: Choi, Kwangmin, et al.
Publicado: (2022) -
Strain Rate during Creep in High-Pressure Die-Cast AZ91 Magnesium Alloys at Intermediate Temperatures
por: Preciado, Mónica, et al.
Publicado: (2019)