Preparation and Characterisation of Polyurethane Acrylate-Based Titanium Dioxide Pigment for Blue Light-Curable Ink

Herein, a polyurethane acrylate-based TiO(2) (PU-TiO(2)) was fabricated using a two-step method. First, a polyurethane prepolymer was prepared. Second, PU-TiO(2) was prepared using amino-modified TiO(2) (A-TiO(2)). The best synthesis process of the polyurethane prepolymer was when the reaction tempe...

Descripción completa

Detalles Bibliográficos
Autores principales: Wang, Chenglong, Qiao, Luyang, Zhai, Qiang, Yan, Kai, Wang, Lili, Zheng, Jinhuan
Formato: Online Artículo Texto
Lenguaje:English
Publicado: MDPI 2021
Materias:
Acceso en línea:https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8624991/
https://www.ncbi.nlm.nih.gov/pubmed/34833274
http://dx.doi.org/10.3390/polym13223977
Descripción
Sumario:Herein, a polyurethane acrylate-based TiO(2) (PU-TiO(2)) was fabricated using a two-step method. First, a polyurethane prepolymer was prepared. Second, PU-TiO(2) was prepared using amino-modified TiO(2) (A-TiO(2)). The best synthesis process of the polyurethane prepolymer was when the reaction temperature was 80 °C, the reaction time was 3 h and the R-value of the polyurethane acrylate was 2. Next, the influence of the A-TiO(2) content on the structure and performance of PU-TiO(2) was examined. The analysis of the rheological properties of the PU-TiO(2) ink indicated that its viscosity gradually increased as the A-TiO(2) content increased. The tensile performance of film improved because of the presence of A-TiO(2). The photo-polymerisation and photo-rheological performance indicated that the PU-TiO(2) structure changed from a hyperbranched structure with TiO(2) as the core to a segmented structure, as the A-TiO(2) content was 3%.