Stress corrosion cracking behavior of 20MnTiB high-strength bolts in simulation of humid climate in Chongqing

20MnTiB steel is the most widely used high-strength bolt material for steel structure bridges in China, and its performance is of great significance to the safe operation of bridges. Based on the investigation of the atmospheric environment in Chongqing in recent years, the corrosion solution to sim...

Descripción completa

Detalles Bibliográficos
Autores principales:	Chen, Lin, Wen, Juan, Zhang, Luyu, Li, Zheng, Li, Guangwen, Ming, Chengwu
Formato:	Online Artículo Texto
Lenguaje:	English
Publicado:	Nature Publishing Group UK 2021
Materias:	Article
Acceso en línea:	https://www.ncbi.nlm.nih.gov/pmc/articles/PMC8669027/ https://www.ncbi.nlm.nih.gov/pubmed/34903777 http://dx.doi.org/10.1038/s41598-021-03302-y

Ejemplares similares

Laboratory-Based Investigation into Stress Corrosion Cracking of Cable Bolts
por: Wu, Saisai, et al.
Publicado: (2019)

High-Strength Bolt Corrosion Fatigue Life Model and Application
por: Hui-li, Wang, et al.
Publicado: (2014)

Crack propagation analysis and fatigue life assessment of high-strength bolts based on fracture mechanics
por: Zhang, Ping, et al.
Publicado: (2023)

Influence of Corrosion on Fatigue of the Fastening Bolts
por: Lachowicz, Maciej B., et al.
Publicado: (2021)

An Eddy Current-Based Structural Health Monitoring Technique for Tracking Bolt Cracking
por: Sun, Hu, et al.
Publicado: (2020)

Odors and Sensations of Humidity and Dryness in Relation to Sick Building Syndrome and Home Environment in Chongqing, China
por: Wang, Juan, et al.
Publicado: (2013)

Investigation on Flexural Fracture Behaviour of Bolted Spherical Joints with Crack Propagation in Screw Threads
por: Shi, Qinghong, et al.
Publicado: (2023)

Repairing Behaviors of Cracked Steel Plates Based on Bolted Fiber-Reinforced Polymer Plates
por: Liu, Jie, et al.
Publicado: (2023)

A Crack Propagation Method for Pipelines with Interacting Corrosion and Crack Defects
por: Xie, Mingjiang, et al.
Publicado: (2022)

Compression Strength of PLA Bolts Produced via FDM
por: Kukla, Mateusz, et al.
Publicado: (2022)

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking
por: Wang, Wenwen, et al.
Publicado: (2015)

The Corrosion Probability and Flexural Strength of an RC Beam under Chloride Ingress Considering the Randomness of Temperature and Humidity
por: Pang, Sen, et al.
Publicado: (2020)

A Study on the Fatigue Performance and Corrosion Resistance of 304/45 Bimetallic Composite Bolts
por: Zhou, Ziming, et al.
Publicado: (2023)

The Effects of Corrosion and Fire Damage on the Steel-Bolted T-Section Connections Used in the Steel Construction
por: Maali, Mahyar, et al.
Publicado: (2023)

The Localized Corrosion and Stress Corrosion Cracking of a 6005A-T6 Extrusion Profile
por: Ma, Jijun, et al.
Publicado: (2021)

Plain washers for high-strength structural bolting, hardened and tempered
por: International Organization for Standardization. Geneva, et al.
Publicado: (1984)

Quantifying Hole-Edge Crack of Bolt Joints by Using an Embedding Triangle Eddy Current Sensing Film
por: Fan, Shilei, et al.
Publicado: (2021)

Microstructure Characterization and Corrosion Resistance of Zinc Coating Obtained on High-Strength Grade 10.9 Bolts Using a New Thermal Diffusion Process
por: Kania, Henryk, et al.
Publicado: (2019)

Experimental Study on Variable-Amplitude Fatigue Performance of M60 High-Strength Bolts of Grid Structures with Bolted Spherical Joints
por: Zhou, Zichun, et al.
Publicado: (2022)

Corrosion Crack Morphology and Creep Analysis of Members Based on Meso-Scale Corrosion Penetration
por: Zeng, Bin, et al.
Publicado: (2022)

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete
por: Ji, Haodong, et al.
Publicado: (2020)

Stress Corrosion Cracking of Additively Manufactured Alloy 625
por: Cabrini, Marina, et al.
Publicado: (2021)

The Influence of Heat Treatment on Corrosion Resistance and Microhardness of Hot-Dip Zinc Coating Deposited on Steel Bolts
por: Jędrzejczyk, Dariusz, et al.
Publicado: (2022)

Effects of Nitrogen and Tensile Direction on Stress Corrosion Cracking Susceptibility of Ni-Free FeCrMnC-Based Duplex Stainless Steels
por: Ha, Heon-Young, et al.
Publicado: (2017)

Automatic crack detection method for loaded coal in vibration failure process
por: Li, Chengwu, et al.
Publicado: (2017)

Mitigation of Galvanic Corrosion in Bolted Joint of AZ31B and Carbon Fiber-Reinforced Composite Using Polymer Insulation
por: Jun, Jiheon, et al.
Publicado: (2021)

Microstructure and Pitting Corrosion of Austenite Stainless Steel after Crack Arrest
por: Zhang, Zhuwu, et al.
Publicado: (2019)

Analysis of the impact of the combined use of rebar bolts and FRP bolts in the roadway enclosure
por: Lyu, Jinguo, et al.
Publicado: (2023)

Effects of pre-oxidation on the corrosion behavior of pure Ti under coexistence of solid NaCl deposit and humid oxygen at 600 °C: the diffusion of chlorine
por: Fan, Lei, et al.
Publicado: (2020)

A Monitoring Method Based on FBG for Concrete Corrosion Cracking
por: Mao, Jianghong, et al.
Publicado: (2016)

Effect of Relative Humidity on Mechanical Degradation of Medium Mn Steels
por: Liu, Qingyang, et al.
Publicado: (2020)

Hexagon bolts for high-strength structural bolting with large width across flats (short thread length): Property classes 8.8 and 10.9
por: International Organization for Standardization. Geneva, et al.
Publicado: (1984)

Effect of Organizational Evolution on the Stress Corrosion Cracking of the Cr-Co-Ni-Mo Series of Ultra-High Strength Stainless Steel
por: Tian, Shuai, et al.
Publicado: (2022)

Influence of Chloride Concentration on Stress Corrosion Cracking and Crevice Corrosion of Austenitic Stainless Steel in Saline Environments
por: Yeh, Chun-Ping, et al.
Publicado: (2020)

Corrosion Behavior and Susceptibility to Stress Corrosion Cracking of Leaded and Lead-Free Brasses in Simulated Drinking Water
por: Choucri, Jamal, et al.
Publicado: (2021)

Effect of Corrosion Temperature on the Corrosion of Q235 Steel and 16Mn Steel in Sodium Aluminate Solutions
por: Quan, Bianli, et al.
Publicado: (2021)

Hexagon bolts for high-strength structural bolting with large width across flats (thread lengths according to 888): Property classes 8.8 and 10.9
por: International Organization for Standardization. Geneva, et al.
Publicado: (1984)

Effect of climate change on outdoor thermal comfort in humid climates
por: Orosa, José A, et al.
Publicado: (2014)

Optimizing Parameters with FEM Model for 20CrMnTi Laser Shocking
por: Sun, Jie, et al.
Publicado: (2022)

Research on the stipe cracking of wine-cap mushroom (Stropharia rugosoannulata) in different humidity conditions
por: Huang, Lei, et al.
Publicado: (2023)

Cannot write session to /tmp/vufind_sessions/sess_n96nrv6hs9mfjao9qp57rga382