Compositional Tailoring of Mg–2Zn–1Ca Alloy Using Manganese to Enhance Compression Response and In-Vitro Degradation

The present study investigates Mg–2Zn–1Ca/XMn alloys as biodegradable implants for orthopedic fracture fixation applications. The effect of the presence and progressive addition of manganese (X = 0.3, 0.5, and 0.7 wt.%) on the degradation, and post-corrosion compressive response were investigated. Results suggest that the addition of manganese at 0.5 wt.% improved the corrosion resistance of Mg–2Zn–1Ca alloys. The pH values stabilized for the 0.5Mn-containing alloy and displayed a lower corrosion rate when compared to other Mg–2Zn–1Ca/Mn alloys. Mg–2Zn–1Ca showed a progressive reduction in the compressive strength properties at the end of day 21 whereas Mg–2Zn–1Ca/0.3Mn and Mg–2Zn–1Ca/0.5Mn samples showed a decrease until day 14 and stabilized around the same strength range after day 21. The ability of Mg–2Zn–1Ca/0.5Mn alloy to develop a network of protective hydroxide and phosphate layers has resulted in the corrosion control of the alloy. Mg–2Zn–1Ca/0.7Mn displays segregation of Mn particles at the grain boundaries resulting in decreased corrosion protection. The mechanism behind the corrosion protection of Mg–2Zn–1Ca alloys was discussed.